標題: | 具3D列印性之熱響應甲基丙烯醯基明膠-聚異丙基丙烯醯胺水凝膠之仿生雙層水凝膠致動器研究 A Biomimetic Bilayer Hydrogel Actuator Based on Thermoresponsive GelMA-PNIPAM Hydrogel with 3D Printability |
其他標題: | A Biomimetic Bilayer Hydrogel Actuator Based on Thermoresponsive GelMA-PNIPAM Hydrogel with 3D Printability |
作者: | 黃于真 Yu-Chen Huang |
指導教授: | 徐善慧 Shan-hui Hsu |
關鍵字: | 致動器,3D列印,熱響應,雙層水凝膠,異丙基丙烯醯胺, actuator,3D printing,thermoresponsive,bilayer hydrogel,N-isopropyl acrylamide, |
出版年 : | 2022 |
學位: | 碩士 |
摘要: | 開發可編程形變的水凝膠系統致動器是一個非常重要的議題,並已引起基礎和應用研究的高度關注。大部分的致動器是不可降解或不能在生理環境下運行的。在此,探索具熱響應和可生物降解的甲基丙烯醯基明膠-聚異丙基丙烯醯胺水凝膠 (即GN水凝膠) 網絡作為雙層水凝膠的主動層。以小角度X光散射顯示GN水凝膠在溫度導致之相變時形成中球體結構 (約230 Å),並由流變數據支持GN水凝膠有三維 (3D) 列印性和可調控的機械性質。通過改變層厚度來優化由主動GN和被動GelMA層組成的雙層水凝膠致動器,以實現曲率約為5.5 cm-1的大、異向性和可重複的彎曲。在塊狀製造的過程中,不同圖案的主動層被設計用於可編程控制的驅動。3D列印的GN水凝膠結構根據其結構設計減少約25-60%的體積,並由37 °C的熱觸發驅動得到更好的解析度,當置於室溫下能完全再次溶脹。更複雜的3D列印蝴蝶致動器展示了通過熱響應來模擬翅膀動作的能力。此外,GN水凝膠中的成肌細胞在14天內表現出約376%的顯著增殖。這項研究為開發用於生物醫學應用的仿生設備、軟機器人和人造肌肉提供一種新的製造策略。 Development of hydrogel-based actuators with programmable deformation is an important issue that arouses high attention in fundamental and applied research. Most of these actuators are non-biodegradable or work under non-physiological conditions. Herein, a thermoresponsive and biodegradable gelatin methacryloyl (GelMA)-poly(N-isopropyl acrylamide) hydrogel (i.e., GN hydrogel) network was explored as the active layer of a bilayer actuator. Small-angle X-ray scattering (SAXS) showed that GN hydrogel formed mesoglobular structures (~ 230 Å) upon thermally induced phase transition. Rheological data supported that GN hydrogel had 3D printability and tunable mechanical properties. A bilayer hydrogel actuator composed of active GN and passive GelMA layers was optimized by varying the layer thickness and compositions to achieve large, anisotropic, and reproducible deformation with a curvature ~ 5.5 cm-1. Different active layer patterns of the bilayer hydrogel were designed for actuation in programmable control. The 3D printed GN hydrogel structures reduced ~ 25-60% volume depending on the structure design and gained better resolution at 37 °C due to thermo-triggered actuation, while were able to fully reswell at room temperature. A more intricate 3D printed butterfly actuator displayed the ability to mimic the wing movement through thermoresponsiveness. In addition, myoblasts laden in GN hydrogel exhibited significant proliferation of ~ 376% in 14 days. This study provides a new fabrication strategy for developing soft robotics, biomimetic devices, and artificial muscles for biomedical applications. |
URI: | http://tdr.lib.ntu.edu.tw/jspui/handle/123456789/83243 |
DOI: | 10.6342/NTU202300060 |
全文授權: | 未授權 |
顯示於系所單位: | 高分子科學與工程學研究所 |
文件中的檔案:
檔案 | 大小 | 格式 | |
---|---|---|---|
ntu-111-1.pdf 目前未授權公開取用 | 5.23 MB | Adobe PDF |
系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。