Title: | 微機電共振器之製作與分析 Fabrication and analysis of MEMS resonator |
Authors: | Ming-Feng Lin 林明鋒 |
Advisor: | 宋家驥(chia-chi Sung) |
Keyword: | 薄膜體聲波共振器,氧化鋅,射頻磁控濺鍍法,氫氧化鉀,反應式離子蝕刻, FBAR,zinc oxide,RF magnetron sputtering,KOH,RIE, |
Publication Year : | 2007 |
Degree: | 碩士 |
Abstract: | 本論文所製作之薄膜體聲波振器由Al/ZnO/Al/Si3N4等不同之薄膜組成,沉積在矽基板(100)上,先利用低壓化學氣相沉積法在矽晶圓兩邊沉積低應力之氮化矽薄膜,一面用來當作薄膜體聲波共振器之支撐層,另一面用來當作氫氧化鉀蝕刻之防護罩,在壓電能作用區下方製作出腔體(cavity),再利用射頻磁控濺鍍法濺鍍壓電層氧化鋅,上下電極使用熱蒸鍍法沉積製作,最後再使用反應式離子蝕刻將腔體內之殘餘矽基板去除,讓共振器下方形成晶界與空氣之介面。
利用X光繞射儀(X-Ray Diffraction, XRD)、掃描式電子顯微鏡(Scanning Electron Microscopy, SEM),針對壓電層氧化鋅作檢測,可發現此薄膜具有C軸(002)之擇優取向,及良好之圓柱狀結構。 最後完成的薄膜體聲波共振器元件之壓電能做作用面積為200×200 μm2,由壓電層氧化鋅、支撐層氮化矽和上下電極鋁所構成,厚度分別為1.54μm、0.2μm、0.1μm、0.1μm。經模擬計算結果,共振頻率為1.86GHz;量測結果為1.27GHz。而實驗結果與討論可提供實驗室一個有價值的參考在未來發展薄膜體聲波共振器之相關研究上。 In this thesis, the Film Bulk Acoustic Resonator (FBAR) has been fabricated by stacking various layers of Al/ZnO/Al/Si3N4 on a silicon substrate (100). The low-stress silicon nitride films were deposited on both side of the substrate by Low-pressure chemical vapor deposition (LPCVD). The upper Si3N4 layer served as a support membrane for the FBAR cantilever, while the bottom layer acted as an etching mask and selectively etched in a KOH (potassium hydroxide) wet etching process to create a cavity under the piezoelectric-active area. The piezoelectric zinc oxide (ZnO) thin film was deposited by reactive RF magnetron sputtering. The bottom and top electrodes are deposited by using thermal evaporation. The underside of the residual silicon was then removed using reactive ion etching (RIE) etching process to create a cavity under the piezoelectric-active area to form a crystal/air interface beneath the resonator. The ZnO film was investigated using x-ray diffractometer (XRD) and scanning electron microscopy (SEM) techniques. The ZnO film showed strongly preferred orientation towards the c-axis, well-textured columnar structure. The FBAR device piezoelectric-active area was 200×200 μm2 which consisted the ZnO film, low-stress Si3N4 membrane, top and bottom Al electrodes with thicknesses of 1.54μm, 0.2μm, 0.1μm, and 0.1μm, respectively. Simulated resonant frequency is 1.86GHz, and measured one is 1.27GHz. The experimental results provided a valuable reference for the future development of FBAR. |
URI: | http://tdr.lib.ntu.edu.tw/jspui/handle/123456789/28824 |
Fulltext Rights: | 有償授權 |
Appears in Collections: | 工程科學及海洋工程學系 |
Files in This Item:
File | Size | Format | |
---|---|---|---|
ntu-96-1.pdf Restricted Access | 3.37 MB | Adobe PDF |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.