請用此 Handle URI 來引用此文件:
http://tdr.lib.ntu.edu.tw/jspui/handle/123456789/83261
完整後設資料紀錄
DC 欄位 | 值 | 語言 |
---|---|---|
dc.contributor.advisor | 林招松 | zh_TW |
dc.contributor.advisor | Chao-Sung Lin | en |
dc.contributor.author | 劉彥均 | zh_TW |
dc.contributor.author | Yen-Chun Liu | en |
dc.date.accessioned | 2023-02-01T17:08:31Z | - |
dc.date.available | 2023-11-09 | - |
dc.date.copyright | 2023-02-01 | - |
dc.date.issued | 2022 | - |
dc.date.submitted | 2022-12-23 | - |
dc.identifier.citation | [1] K. K. Sankaran and R. S. Mishra, Metallurgy and Design of Alloys with Hierarchical Microstructures. Elsevier, 2017.
[2] "Electron Backscatter Diffraction Analysis." http://www.ebsd.com/ebsdexplained/principle-components-of-an-ebsd-system (accessed 1 December 2017). [3] X. Dong, "Surface treatments for magnesium alloys," Handbook of Manufacturing Engineering and Technology, pp. 3031-3054, 2015. [4] "Binary Phase Diagrams," in Alloy Phase Diagrams, vol. 3, H. Okamoto, M. E. Schlesinger, and E. M. Mueller Eds.: ASM International, 2016, p. 0. [5] E. A. Starke Jr and J. T. Staley, "Application of modern aluminum alloys to aircraft," Progress in aerospace sciences, vol. 32, no. 2-3, pp. 131-172, 1996. [6] R. S. Mishra and Z. Ma, "Friction stir welding and processing," Materials science and engineering: R: reports, vol. 50, no. 1-2, pp. 1-78, 2005. [7] I. Milošev and G. Frankel, "conversion coatings based on zirconium and/or titanium," Journal of The Electrochemical Society, vol. 165, no. 3, p. C127, 2018. [8] G. Song and A. Atrens, "Understanding magnesium corrosion—a framework for improved alloy performance," Advanced engineering materials, vol. 5, no. 12, pp. 837-858, 2003. [9] T. He, W. Shi, S. Xiang, C. Huang, and R. G. Ballinger, "Influence of Aging on Corrosion Behaviour of the 6061 Cast Aluminium Alloy," Materials, vol. 14, no. 8, p. 1821, 2021. [10] V. Firouzdor and S. Kou, "Formation of liquid and intermetallics in Al-to-Mg friction stir welding," Metallurgical and Materials Transactions A, vol. 41, no. 12, pp. 3238-3251, 2010. [11] V. Firouzdor and S. Kou, "Al-to-Mg friction stir welding: effect of material position, travel speed, and rotation speed," Metallurgical and Materials Transactions A, vol. 41, no. 11, pp. 2914-2935, 2010. [12] G. Williams and H. N. McMurray, "Localized corrosion of magnesium in chloride-containing electrolyte studied by a scanning vibrating electrode technique," Journal of the electrochemical Society, vol. 155, no. 7, p. C340, 2008. [13] N. Yamamoto, J. Liao, S. Watanabe, and K. Nakata, "Effect of intermetallic compound layer on tensile strength of dissimilar friction-stir weld of a high strength Mg alloy and Al alloy," Materials transactions, vol. 50, no. 12, pp. 2833-2838, 2009. [14] D. Maisonnette, M. Suery, D. Nelias, P. Chaudet, and T. Epicier, "Effects of heat treatments on the microstructure and mechanical properties of a 6061 aluminium alloy," Materials Science and Engineering: A, vol. 528, no. 6, pp. 2718-2724, 2011. [15] M. Taheri, J. Kish, N. Birbilis, M. Danaie, E. A. McNally, and J. R. McDermid, "Towards a physical description for the origin of enhanced catalytic activity of corroding magnesium surfaces," Electrochimica Acta, vol. 116, pp. 396-403, 2014. [16] F. Andreatta, A. Turco, I. De Graeve, H. Terryn, J. De Wit, and L. Fedrizzi, "SKPFM and SEM study of the deposition mechanism of Zr/Ti based pre-treatment on AA6016 aluminum alloy," Surface and coatings Technology, vol. 201, no. 18, pp. 7668-7685, 2007. [17] S. Verdier, N. van der Laak, F. Dalard, J. Metson, and S. Delalande, "An electrochemical and SEM study of the mechanism of formation, morphology, and composition of titanium or zirconium fluoride-based coatings," Surface and Coatings Technology, vol. 200, no. 9, pp. 2955-2964, 2006. [18] O. Kayode and E. T. Akinlabi, "An overview on joining of aluminium and magnesium alloys using friction stir welding (FSW) for automotive lightweight applications," Materials Research Express, vol. 6, no. 11, p. 112005, 2019. [19] A. Simar and M.-N. Avettand-Fènoël, "State of the art about dissimilar metal friction stir welding," Science and Technology of Welding and Joining, vol. 22, no. 5, pp. 389-403, 2017. [20] V. Paradiso, F. Rubino, P. Carlone, and G. Palazzo, "Magnesium and aluminium alloys dissimilar joining by friction stir welding," Procedia Engineering, vol. 183, pp. 239-244, 2017. [21] L. Shah, N. Othman, and A. Gerlich, "Review of research progress on aluminium–magnesium dissimilar friction stir welding," Science and Technology of Welding and Joining, vol. 23, no. 3, pp. 256-270, 2018. [22] Y. Liu et al., "Protection of AA5083 by a zirconium-based conversion coating," Journal of The Electrochemical Society, vol. 163, no. 9, p. C576, 2016. [23] A. Yi, W. Li, J. Du, and S. Mu, "Preparation and properties of chrome-free colored Ti/Zr based conversion coating on aluminum alloy," Applied Surface Science, vol. 258, no. 16, pp. 5960-5964, 2012. [24] S. S. Golru, M. Attar, and B. Ramezanzadeh, "Morphological analysis and corrosion performance of zirconium based conversion coating on the aluminum alloy 1050," Journal of Industrial and Engineering Chemistry, vol. 24, pp. 233-244, 2015. [25] M. Esmaily et al., "Fundamentals and advances in magnesium alloy corrosion," Progress in Materials Science, vol. 89, pp. 92-193, 2017. [26] B. Carlson and J. Jones, "The Metallurgical Aspects of the Corrosion Behaviour of Cast Mg--Al Alloys," Light Metals Processing and Applications, pp. 833-847, 1993. [27] G.-L. Song and Z. Xu, "The surface, microstructure and corrosion of magnesium alloy AZ31 sheet," Electrochimica acta, vol. 55, no. 13, pp. 4148-4161, 2010. [28] S. Pawar, X. Zhou, G. Thompson, G. Scamans, and Z. Fan, "The role of intermetallics on the corrosion initiation of twin roll cast AZ31 Mg alloy," Journal of The Electrochemical Society, vol. 162, no. 9, p. C442, 2015. [29] G. Song and A. Atrens, "Magnesium corrosion mechanisms," Corrosion Science and Technology, vol. 31, no. 2, 2002. [30] M. G. Acharya and A. N. Shetty, "The corrosion behavior of AZ31 alloy in chloride and sulfate media–a comparative study through electrochemical investigations," Journal of Magnesium and Alloys, vol. 7, no. 1, pp. 98-112, 2019. [31] S. Pawar, X. Zhou, T. Hashimoto, G. Thompson, G. Scamans, and Z. Fan, "Investigation of the microstructure and the influence of iron on the formation of Al8Mn5 particles in twin roll cast AZ31 magnesium alloy," Journal of Alloys and Compounds, vol. 628, pp. 195-198, 2015. [32] J. H. Nordlien, S. Ono, N. Masuko, and K. Nis, "Morphology and structure of oxide films formed on magnesium by exposure to air and water," Journal of the Electrochemical Society, vol. 142, no. 10, p. 3320, 1995. [33] M. Taheri, R. Phillips, J. Kish, and G. Botton, "Analysis of the surface film formed on Mg by exposure to water using a FIB cross-section and STEM–EDS," Corrosion Science, vol. 59, pp. 222-228, 2012. [34] J. H. Nordlien, K. NişancioǦu, S. Ono, and N. Masuko, "Morphology and structure of oxide films formed on MgAl alloys by exposure to air and water," Journal of the Electrochemical Society, vol. 143, no. 8, p. 2564, 1996. [35] R. L. Petty, A. W. Davidson, and J. Kleinberg, "The anodic oxidation of magnesium metal: evidence for the existence of unipositive magnesium1, 2," Journal of the American Chemical Society, vol. 76, no. 2, pp. 363-366, 1954. [36] A. Atrens, G. L. Song, M. Liu, Z. Shi, F. Cao, and M. S. Dargusch, "Review of recent developments in the field of magnesium corrosion," Advanced Engineering Materials, vol. 17, no. 4, pp. 400-453, 2015. [37] S. Salleh, S. Thomas, J. Yuwono, K. Venkatesan, and N. Birbilis, "Enhanced hydrogen evolution on Mg (OH) 2 covered Mg surfaces," Electrochimica Acta, vol. 161, pp. 144-152, 2015. [38] D. Lysne, S. Thomas, M. Hurley, and N. Birbilis, "On the Fe enrichment during anodic polarization of Mg and its impact on hydrogen evolution," Journal of the Electrochemical Society, vol. 162, no. 8, p. C396, 2015. [39] S. Fajardo and G. Frankel, "Effect of impurities on the enhanced catalytic activity for hydrogen evolution in high purity magnesium," Electrochimica Acta, vol. 165, pp. 255-267, 2015. [40] A. C. Alfrey, "Aluminum," Advances in clinical chemistry, vol. 23, pp. 69-91, 1983. [41] Y. Wu and H. Liao, "Corrosion behavior of extruded near eutectic Al–Si–Mg and 6063 alloys," Journal of materials science & technology, vol. 29, no. 4, pp. 380-386, 2013. [42] G. Sha, K. O’Reilly, B. Cantor, J. Titchmarsh, and R. Hamerton, "Quasi-peritectic solidification reactions in 6xxx series wrought Al alloys," Acta Materialia, vol. 51, no. 7, pp. 1883-1897, 2003. [43] G. Sha, K. O’Reilly, B. Cantor, J. Worth, and R. Hamerton, "Growth related metastable phase selection in a 6xxx series wrought Al alloy," Materials Science and Engineering: A, vol. 304, pp. 612-616, 2001. [44] S. Andersen, H. Zandbergen, J. Jansen, C. TrÆholt, U. Tundal, and O. Reiso, "The crystal structure of the β ″phase in Al–Mg–Si alloys," Acta Materialia, vol. 46, no. 9, pp. 3283-3298, 1998. [45] Z. Zhang et al., "Corrosion Behaviors of AA5083 and AA6061 in Artificial Seawater: Effects of Cl-, HSO3-and Temperature," Int. J. Electrochem. Sci., vol. 15, pp. 1218-1229, 2020. [46] X. He, F. Gu, and A. Ball, "A review of numerical analysis of friction stir welding," Progress in Materials Science, vol. 65, pp. 1-66, 2014. [47] M. Fuller, S. Swaminathan, A. Zhilyaev, and T. McNelley, "Microstructural transformations and mechanical properties of cast NiAl bronze: Effects of fusion welding and friction stir processing," Materials Science and Engineering: A, vol. 463, no. 1-2, pp. 128-137, 2007. [48] L. Liu, D. Ren, and F. Liu, "A review of dissimilar welding techniques for magnesium alloys to aluminum alloys," Materials, vol. 7, no. 5, pp. 3735-3757, 2014. [49] Y. S. Sato, S. H. C. Park, M. Michiuchi, and H. Kokawa, "Constitutional liquation during dissimilar friction stir welding of Al and Mg alloys," Scripta Materialia, vol. 50, no. 9, pp. 1233-1236, 2004. [50] A. Somasekharan and L. Murr, "Microstructures in friction-stir welded dissimilar magnesium alloys and magnesium alloys to 6061-T6 aluminum alloy," Materials Characterization, vol. 52, no. 1, pp. 49-64, 2004. [51] J. Yan, Z. Xu, Z. Li, L. Li, and S. Yang, "Microstructure characteristics and performance of dissimilar welds between magnesium alloy and aluminum formed by friction stirring," Scripta Materialia, vol. 53, no. 5, pp. 585-589, 2005. [52] Y. Sato, A. Shiota, H. Kokawa, K. Okamoto, Q. Yang, and C. Kim, "Effect of interfacial microstructure on lap shear strength of friction stir spot weld of aluminium alloy to magnesium alloy," Science and Technology of Welding and Joining, vol. 15, no. 4, pp. 319-324, 2010. [53] A. McLean, G. Powell, I. Brown, and V. Linton, "Friction stir welding of magnesium alloy AZ31B to aluminium alloy 5083," Science and Technology of Welding and Joining, vol. 8, no. 6, pp. 462-464, 2003. [54] S. A. Khodir and T. Shibayanagi, "Dissimilar friction stir welded joints between 2024-T3 aluminum alloy and AZ31 magnesium alloy," Materials transactions, vol. 48, no. 9, pp. 2501-2505, 2007. [55] Y. Kwon, I. Shigematsu, and N. Saito, "Dissimilar friction stir welding between magnesium and aluminum alloys," Materials Letters, vol. 62, no. 23, pp. 3827-3829, 2008. [56] V. Firouzdor and S. Kou, "Al-to-Mg friction stir welding: effect of positions of Al and Mg with respect to the welding tool," Welding Journal, vol. 88, no. 11, pp. 213-224, 2009. [57] M. Azizieh, A. S. Alavijeh, M. Abbasi, Z. Balak, and H. Kim, "Mechanical properties and microstructural evaluation of AA1100 to AZ31 dissimilar friction stir welds," Materials Chemistry and Physics, vol. 170, pp. 251-260, 2016. [58] R. Beygi et al., "The inhibitory effect of stir zone liquefaction and eutectic-phase formation on the growth of γ/β intermetallics during dissimilar FSW of Al/Mg alloys," Journal of Manufacturing Processes, vol. 70, pp. 152-162, 2021. [59] X. Liu, J. Cui, X. Wu, Y. Guo, and J. Zhang, "Phase growth in diffusion couples under an low frequency alternating magnetic field," Scripta materialia, vol. 52, no. 1, pp. 79-82, 2005. [60] S. Verdier, S. Delalande, N. Van Der Laak, J. Metson, and F. Dalard, "Monochromatized x‐ray photoelectron spectroscopy of the AM60 magnesium alloy surface after treatments in fluoride‐based Ti and Zr solutions," Surface and Interface Analysis: An International Journal devoted to the development and application of techniques for the analysis of surfaces, interfaces and thin films, vol. 37, no. 5, pp. 509-516, 2005. [61] T. Schram, G. Goeminne, H. Terryn, W. Vanhoolst, and P. Van Espen, "Study of the composition of zirconium based chromium free conversion layers on aluminium," Transactions of the IMF, vol. 73, no. 3, pp. 91-95, 1995. [62] W. Fang and C.-Y. Lo, "On the thermal expansion coefficients of thin films," Sensors and Actuators A: Physical, vol. 84, no. 3, pp. 310-314, 2000. [63] M. Hu, M. D. Thouless, and A. G. Evans, "The decohesion of thin films from brittle substrates," Acta Metallurgica, vol. 36, no. 5, pp. 1301-1307, 1988. [64] W. M. Haynes, CRC Handbook of Chemistry and Physics, 95th Edition., 95 Edition ed. Boca Raton: Hoboken : CRC Press, 2014, 2014, p. 2704. [65] Y. Yang, F. Scenini, and M. Curioni, "A study on magnesium corrosion by real-time imaging and electrochemical methods: relationship between local processes and hydrogen evolution," Electrochimica acta, vol. 198, pp. 174-184, 2016. [66] E. Michailidou, H. McMurray, and G. Williams, "Quantifying the role of transition metal electrodeposition in the cathodic activation of corroding magnesium," Journal of the Electrochemical Society, vol. 165, no. 5, p. C195, 2018. | - |
dc.identifier.uri | http://tdr.lib.ntu.edu.tw/jspui/handle/123456789/83261 | - |
dc.description.abstract | 本研究使用的材料為AZ31B鎂合金與6061-T6鋁合金進行摩擦攪拌異質焊接,第一部份的研究著重於利用SEM進行焊接後的微結構分析,並搭配XRD與EBSD進行焊道區的相鑑定。將拋光完後的試片分為焊道外鎂、鋁基材的表面形貌以及焊道區的表面形貌進行討論,其中焊道區內又分為四個部分,分別是二次相、介金屬相、焊道區的鎂、焊道區的鋁。焊道區的二次相含有來自6061鋁合金的鋁鐵矽相、鎂矽相以及來自AZ31鎂合金的鋁錳相,由SEM的結果顯示,在焊道區可以觀察到二次相大量聚集或是呈現帶狀分布的現象,而這些二次相的成分以鋁鐵矽相與鎂矽相為主,較少觀察到鋁錳相。介金屬相為Al3Mg2和Al12Mg17,由鋁鎂原子的交互擴散所形成,在焊道內可觀察到相的分布符合擴散理論,與鋁相連的介金屬相為Al3Mg2,與鎂相連的為Al12Mg17,而Al12Mg17 +Mg兩相共存區的出現則說明此摩擦攪拌焊接試片非典型的二元擴散偶。焊道區內的鋁和鎂則和焊道外的鋁和鎂表面形貌相同。
第二部分著重於六氟鋯酸化成後的微結構分析,並提出於焊道區內的成膜機制。在鋁鐵矽相以及鋁錳相等比基材鈍態的二次相上可以觀察到較厚的化成膜。在介金屬相的部份,Al12Mg17比起Al3Mg2表面有較多白色的鋯顆粒,Al12Mg17 +Mg兩相共存區表面也覆蓋白色的鋯顆粒,鎂的表面可觀察到棉絮狀的鋯顆粒,鋁的表面則相較於其他相較平整。經由TEM的分析顯示,化成膜為雙層結構,外層推測為ZrO2、內層則為金屬氧化物,其中Al12Mg17 和Mg的金屬氧化物內含有氟的成分。在膜層厚度的部份,ZrO2膜層厚度Al12Mg17 > Mg> Al3Mg2 ≅Al,氧化層厚度Mg > Al12Mg17> Al3Mg2 > Al。最後基於化成後表面微結構影像、TEM化成膜成分與厚度分析提出了成膜機制。 | zh_TW |
dc.description.abstract | The material used in this study is AZ31B magnesium alloy and 6061-T6 aluminum alloy of friction stir welding. The first part of the study focuses on the microstructure analysis after welding, while XRD and EBSD are used for phase indentification in the stir zone. The discussion of surface morphology is divided into three sections: magnesium substrate, aluminum substrate and stir zone. Among which the stir zone area was further divided into four parts, namely secondary phase, intermetallic compounds, magnesium in stir zone, and aluminum in stir zone. The second phase in the stir zone contains Al-Fe-Si and Mg-Si phases from 6061 aluminum alloy, and Al-Mn phase from AZ31 magnesium alloy. The SEM results indicate that aggregation of second phases can be observed in the stir zone, which are mainly Al-Fe-Si and Mg-Si phases, whereas Al-Mn phase is rarely observed. The intermetallic compounds are Al3Mg2 and Al12Mg17, which are formed by diffusion of Al and Mg atoms. The distribution of the phases in the stir zone is in accordance with the diffusion theory, where the intermetallic compound adjacent to Al is Al3Mg2 and the intermetallic compound adjacent to Mg is Al12Mg17. The surface morphology of Al and Mg in the stir zone is similar as that of Al and Mg outside the stir zone.
The second part of the study focuses on the microstructure analysis after conversion coating. Thicker films are observed on the Al-Fe-Si and Al-Mn second phases which are more noble compared to the base material. The surface of Al12Mg17 has more white Zr particles than that of Al3Mg2, and the two phase region of Al12Mg17 +Mg is also covered with Zr white particles. Cotton-like Zr particles can be observed on the surface of Mg, while the surface of Al is relatively smooth compared to others.The TEM analysis shows that the conversion coating film is a two-layer structure, the outer layer is speculated to be ZrO2 and the inner layer is metal oxide. It is observed that the metal oxide layers of Al12Mg17 and Mg contain fluorine. The thickness of ZrO2 layer is Al12Mg17 > Mg > Al3Mg2 ≅ Al, and the thickness of metal oxide layer is Mg > Al12Mg17 > Al3Mg2 > Al. Al last, a film formation mechanism was proposed based on the microstructure image and TEM analysis of the composition and thickness after conversion coating. | en |
dc.description.provenance | Submitted by admin ntu (admin@lib.ntu.edu.tw) on 2023-02-01T17:08:31Z No. of bitstreams: 0 | en |
dc.description.provenance | Made available in DSpace on 2023-02-01T17:08:31Z (GMT). No. of bitstreams: 0 | en |
dc.description.tableofcontents | 摘要 i
ABSTRACT ii 誌謝 iv 總目錄 v 圖目錄 viii 表目錄 xiii 第一章 前言 1 第二章 文獻回顧 3 2.1 鎂合金 3 2.1.1 概述 3 2.1.2 AZ31B鎂合金簡介 5 2.1.3 AZ31的二次相 6 2.1.4 純鎂與鎂鋁合金表面氧化層 6 2.1.5 負差值效應 8 2.2 鋁合金 11 2.2.1 概述 11 2.2.2 鋁合金的命名 12 2.2.3 6061鋁合金簡介 14 2.2.4 鋁-鎂-矽合金的析出強化與二次相 14 2.2.5 6061鋁合金二次相的腐蝕 18 2.3 鎂鋁摩擦攪拌焊接(Friction Stir Welding) 19 2.3.1 摩擦攪拌焊接原理 19 2.3.2 FSW焊接微結構 20 2.3.3 介金屬化合物形成機制 24 2.4 化成處理 27 2.4.1 鎂合金鋯化成 29 2.4.2 鋁合金鋯化成 31 第三章 實驗步驟與方法 34 3.1 實驗流程 34 3.2 試片製備 35 3.2.1 實驗材料與藥品 35 3.2.2 試片研磨與拋光 36 3.2.3 化成處理 36 3.3 微結構分析與方法 37 3.3.1 光學顯微鏡(OM) 37 3.3.2 掃描式電子顯微鏡(SEM) 37 3.3.3 能量散射X射線譜 (EDS) 38 3.3.4 背向散射電子繞射(EBSD) 38 3.3.5 穿透式電子顯微鏡(TEM) 39 3.3.6 掃描穿透式電子顯微鏡(STEM) 40 3.3.7 X光繞射儀(XRD) 40 第四章 實驗結果與討論 41 4.1 鋁鎂合金摩擦攪拌焊接之拋光後分析 41 4.1.1 焊道外基材表面形貌影像觀察 41 4.1.2 焊道區表面形貌觀察 43 4.1.3 焊道區之相鑑定 63 4.2 鋯化成後之微結構分析 65 4.2.1 焊道外基材表面形貌觀察 65 4.2.2 焊道表面形貌觀察 68 4.2.3 焊道區橫截面影像觀察 79 4.3 鋯化成成膜機制討論 98 第五章 結論 103 第六章 未來展望 105 參考文獻 106 | - |
dc.language.iso | zh_TW | - |
dc.title | AZ31B鎂合金與6061鋁合金摩擦攪拌焊接材料之六氟鋯酸化成處理 | zh_TW |
dc.title | Hexafluorozirconate Conversion Coating on AZ31B and 6061 Friction Stir Welding | en |
dc.title.alternative | Hexafluorozirconate Conversion Coating on AZ31B and 6061 Friction Stir Welding | - |
dc.type | Thesis | - |
dc.date.schoolyear | 111-1 | - |
dc.description.degree | 碩士 | - |
dc.contributor.oralexamcommittee | 林新智;林景崎;李岳聯;蔡文達 | zh_TW |
dc.contributor.oralexamcommittee | Hsin-Chih Lin;Jing-Chie Lin;Yueh-Lien Lee;Wen-Ta Tsai | en |
dc.subject.keyword | AZ31鎂合金,6061鋁合金,摩擦攪拌焊接,鋯化成,微結構,成膜機制, | zh_TW |
dc.subject.keyword | AZ31B,6061,frition stir welding,zirconium conversion coating,microstructure,film formation, | en |
dc.relation.page | 111 | - |
dc.identifier.doi | 10.6342/NTU202210146 | - |
dc.rights.note | 未授權 | - |
dc.date.accepted | 2022-12-26 | - |
dc.contributor.author-college | 工學院 | - |
dc.contributor.author-dept | 材料科學與工程學系 | - |
顯示於系所單位: | 材料科學與工程學系 |
文件中的檔案:
檔案 | 大小 | 格式 | |
---|---|---|---|
U0001-0649221218427090.pdf 目前未授權公開取用 | 11.45 MB | Adobe PDF |
系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。