Abstract

本研究成功開發出在大氣環境下利用自動化機構燒結出局部活化碳纖維，探討了不同的燒結溫度、燒結時間，C80 (700℃燒結80分鐘)和緊貼著碳纖維的方式有最大的比表面積68.39 m^2/g和單束碳纖維比電容值7.47 F/g，PVdF膠體電解質(gel polymer electrolyte) 組裝成灌注(2 cm x 2 cm)超級電容後，進行充放電測試在2 mA/g下擁有最大之電容值2.6 F/g以及90 %以上的庫倫效率，確定了活化程序後將局部活化碳纖維組裝成5 cm x 5 cm (活性面積3 cm x 3 cm)一體超級電容，在製程上利用氟碳樹脂有效的抵擋了環氧樹脂的侵入，也成功製作出能夠承受附載的「結構一體超級電容」，但因封裝後環氧樹脂可能與PVdF膠體電解質(gel polymer electrolyte)有些微碰處導致原先的官能基反應消失，從交流阻抗圖可以明顯地發現到，在未封裝前是有一個半圓(Rct)存在，代表有化學反應存在，而封裝後半圓消失，使得原先尚未封裝的比電容值從1.4 F/g 降至1.0 F/g，成功製作出規模化串接一體多功能複合材料，在實際應用上可使LED燈發亮持續超過20分鐘，小風扇轉動約1分鐘。

In this study, the local activated carbon fiber was successfully sintering by using the automated structure in the atmosphere, and the different sintering temperature and sintering time were discussed. The C80 (700℃ sintering for 80 minutes) and the carbon fiber had the largest specific surface area of 68.39 m^2/g and singular carbon fiber specific capacitance 7.47 F/g, PVdF gel polymer electrolyte assembled into a Perfusion(2 cm x 2 cm) supercapacitor. The charge and discharge test has a maximum capacitance of 2.6 F/g at 2 mA/g and More than 90% of the Coulomb efficiency, after the activation procedure, the locally activated carbon fiber was assembled into a 5 cm x 5 cm (active area 3 cm x 3 cm) Unibody supercapacitor, and the fluorocarbon resin was used to effectively resist the intrusion of epoxy resin in the process. Successfully produced a 'structural Unibody supercapacitor' that can withstand the loading, but since the epoxy resin may be slightly contact the PVdF gel polymer electrolyte after encapsulation. The original functional group reaction disappears, and the AC impedance can be clearly It was found that there is a semicircle (Rct) before the package, which means that there is a chemical reaction. The semicircle disappears after encapsulation, which makes the original specific capacitance that has not been packaged first is reduced from 1.4 F/g to 0.9 F/g. Successfully produced a large-scale serial multifunctional composite material. In practical applications, the LED light can be illuminated for more than 20 minutes, and the small fan is rotated for about 1 minute.