請用此 Handle URI 來引用此文件:
http://tdr.lib.ntu.edu.tw/jspui/handle/123456789/51686
完整後設資料紀錄
DC 欄位 | 值 | 語言 |
---|---|---|
dc.contributor.advisor | 林招松 | |
dc.contributor.author | Chien-Hao Wang | en |
dc.contributor.author | 王建豪 | zh_TW |
dc.date.accessioned | 2021-06-15T13:44:34Z | - |
dc.date.available | 2020-12-21 | |
dc.date.copyright | 2015-12-21 | |
dc.date.issued | 2015 | |
dc.date.submitted | 2015-12-03 | |
dc.identifier.citation | 1. Karbasian, H. and A.E. Tekkaya, A review on hot stamping. Journal of Materials Processing Technology, 2010. 210(15): p. 2103-2118.
2. Bariani, P.F., et al., Testing formability in the hot stamping of HSS. Cirp Annals-Manufacturing Technology, 2008. 57(1): p. 265-268. 3. Fan, D.W., et al., Influence of Isothermal Deformation Conditions on The Mechanical Properties of 22MnB5 HPF Steel. Steel Research International, 2010. 81(4): p. 292-298. 4. Lee, C.W., et al., Liquid-Metal-Induced Embrittlement of Zn-Coated Hot Stamping Steel. Metallurgical and Materials Transactions A, 2012. 43(13): p. 5122-5127. 5. Merklein, A. and J. Lechler, Investigation of the thermo-mechanical properties of hot stamping steels. Journal of Materials Processing Technology, 2006. 177(1-3): p. 452-455. 6. Fan, D.W., et al., Coating Degradation in Hot Press Forming. Isij International, 2010. 50(4): p. 561-568. 7. Jenner, F., et al., Evolution of Phases, Microstructure, and Surface Roughness during Heat Treatment of Aluminized Low Carbon Steel. Metallurgical and Materials Transactions a-Physical Metallurgy and Materials Science, 2010. 41A(6): p. 1554-1563. 8. Kondratiuk, J., et al., Zinc coatings for hot sheet metal forming: Comparison of phase evolution and microstructure during heat treatment. Surface & Coatings Technology, 2011. 205(17-18): p. 4141-4153. 9. Fan, D.W. and B.C. De Cooman, State-of-the-Knowledge on Coating Systems for Hot Stamped Parts. Steel Research International, 2012. 83(5): p. 412-433. 10. Autengruber, R., et al., Surface and Coating Analysis of Press-Hardened Hot-Dip Galvanized Steel Sheet. Steel Research International, 2012. 83(11): p. 1005-1011. 11. Marder, A.R., The metallurgy of zinc-coated steel. Progress in Materials Science, 2000. 45(3): p. 191-271. 12. Raghavan, V., Fe-Zn (Iron-Zinc). Journal of Phase Equilibria, 2003. 24: p. 544-545. 13. Ghuman, A. and J. Goldstein, Reaction Mechanisms for the Coatings Formed During the Hot Dipping of Iron in 0 to 10 pct Al-Zn baths at 450 to 700 C. Metallurgical Transactions, 1971. 2(10): p. 2903-2914. 14. Kuziak, R., R. Kawalla, and S. Waengler, Advanced high strength steels for automotive industry. Archives of civil and mechanical engineering, 2008. 8(2): p. 103-117. 15. Wagoner, R.H. and G.R. Smith, Advanced High Strength Steel Workshop. Arlington, Virginia, USA, 2006: p. 1-122. 16. Demeri, M.Y., Advanced high-strength steels : science, technology, and applications. 2013: p. p. 48. 17. Wormuth, R., ECSC Project 7210-PR/121. Final Report, 2002. 18. Hertveldt, I., B. De Cooman, and S. Claessens, Influence of annealing conditions on the galvanizability and galvannealing properties of TiNb interstitial-free steels, strengthened with phosphorous and manganese. Metallurgical and materials transactions A, 2000. 31(4): p. 1225-1232. 19. Jordan, C. and A. Marder, Fe-Zn phase formation in interstitial-free steels hot-dip galvanized at 450° C: Part I 0.00 wt% Al-Zn baths. Journal of Materials Science, 1997. 32(21): p. 5593-5602. 20. L.G. Garza, C.J.V.T., The effect of ζ -phase on the Frictional Behavior of galvannealed interstitial free sheet steels, in Galvatech'07. 2007. p. 248-253. 21. T. Takasugi, J.M., Plastic Deformation and Fracture Behavior of Galvannealed Coating under Compressive Stress Circumstance, in Galvatech'07. 2007. p. 230-235. 22. Mataign, J.M., Key Mechanisms in Galvanization of Steel Sheets, in Galvatech'07. 2007. p. 333-338. 23. Nunomura, Y. and T. Takasugi, Plastic deformation and fracture behavior of galvannealed coating. ISIJ international, 2003. 43(3): p. 454-460. 24. Nakamori, T., et al., Coating adhesion and interface structure of galvannealed steel. Isij International, 1995. 35(12): p. 1494-1501. 25. C.E. Jordan, K.M.G., A.O. Benscoter, A.R. Marder, Metallographic preparation technique for hot-dip galvanized and galvannealed coatings on steel. Materials Characterization, 1993. 31: p. 107–114. 26. Kilpatrick, J.R., A New Etching Technique for Galvanneal and Hot-Dipped Galvanized Coatings. Praktische Metallographie, 1991. 28: p. 649-658. 27. CHENG, C.S.L.M.M.a.C.C., Phase Evolution in Galvanneal Coatings on Steel Sheets. ISIJ International, 1995. 35: p. 503-511. 28. K.C. Lin, P.W.C., C.S. Lin, and H.B. Chen, Galvanizing and Galvannealing Behavior of CMnSiCr Dual-Phase Steels. METALLURGICAL AND MATERIALS TRANSACTIONS A, 2013. 44A: p. 2690-2698. 29. Gittings, D., D. Rowland, and J. Mack. Effect of Bath Composition on Aluminum Coatings on Steel. in 32nd Annual Convention of the American Society for Metals. 1951. 30. Eggeler, G., W. Auer, and H. Kaesche, On the influence of silicon on the growth of the alloy layer during hot dip aluminizing. Journal of Materials Science, 1986. 21(9): p. 3348-3350. 31. Kwon, S. and J. Lee, Interface Morphology Between the Aluminide Layer and Iron Substrate in the Hot-Dip Aluminizing Process. Canadian Metallurgical Quarterly, 1981. 20(3): p. 351-357. 32. Bahadur, A. and O. Mohanty, Structural studies of hot dip aluminized coatings on mild steel. Materials Transactions, JIM, 1991. 32(11): p. 1053-1061. 33. Shady, M., et al., On the technological properties of steel strips aluminized in Al-Si baths. Journal of materials science letters, 1996. 15(12): p. 1032-1036. 34. Khalifa, W., F. Samuel, and J. Gruzleski, Iron intermetallic phases in the Al corner of the Al-Si-Fe system. Metallurgical and Materials Transactions A, 2003. 34(3): p. 807-825. 35. Birks, N., G.H. Meier, and F.S. Pettit, Introduction to the high temperature oxidation of metals. 2006: Cambridge University Press. 36. Gaskell, D.R., Introduction to the Thermodynamics of Materials. 2008: CRC Press. 37. Xu, C. and W. Gao, Pilling-Bedworth ratio for oxidation of alloys. Material Research Innovations, 2000. 3(4): p. 231-235. 38. Fontana, M.G., Corrosion engineering. 2005: Tata McGraw-Hill Education. 39. McCafferty, E., Introduction to corrosion science. 2010: Springer Science & Business Media. 40. C.W. Lee, D.W.F., S.J. Leem Il R. Sohn, and B.C. De Cooman, Galvanized caoting evolution during hot stamping. in Galvantexh '11: 8th International Conference on Zinc and Zinc Alloy Coated Steel, 2011. 41. Balluffi, R.W., S. Allen, and W.C. Carter, Kinetics of materials. 2005: John Wiley & Sons. 42. Boggs, W.E., The Oxidation of Iron‐Aluminum Alloys from 450° to 900° C. Journal of the Electrochemical Society, 1971. 118(6): p. 906-913. 43. Hagel, W., The Oxidation off Iron, Nickel and Cobalt-Base Alloys Containing Aluminum. Corrosion, 1965. 21(10): p. 316-326. 44. Trunov, M.A., et al., Effect of polymorphic phase transformations in Al 2 O 3 film on oxidation kinetics of aluminum powders. Combustion and Flame, 2005. 140(4): p. 310-318. 45. Perrot, P., J.-C. Tissier, and J.-Y. Dauphin, Stable and metastable equilibria in the Fe-Zn-Al system at 450 C. Zeitschrift für Metallkunde, 1992. 83(11): p. 786-790. 46. Zhou, B., et al., Microstructure and Oxidation of 55% Al-Zn-Si Hot-Dip Coatings Deposited on Low Carbon Steel at High Temperature. Advanced Materials Research, 2012. 399: p. 1998-2003. 47. P. Drillet, R.G., G. Leuiller, Study of cracks propagation inside the steel on press hardened steel zinc based coatings. in Galvatech '11: 8th International Conference on Zinc and Zinc Alloy Coated Steel, 2011. 48. Fernandes, P. and D. Jones, Mechanisms of liquid metal induced embrittlement. International materials reviews, 1997. 42(6): p. 251-261. 49. Nicholas, M. and C. Old, Liquid metal embrittlement. Journal of Materials Science, 1979. 14(1): p. 1-18. 50. Wang, K.-K., et al., Role of Al in Zn bath on the formation of the inhibition layer during hot-dip galvanizing for a 1.2 Si–1.5 Mn transformation-induced plasticity steel. Applied surface science, 2013. 285: p. 458-468. 51. Blumenau, M., et al., Impact of selective oxidation during inline annealing prior to hot-dip galvanizing on Zn wetting and hydrogen-induced delayed cracking of austenitic FeMnC steel. Surface and Coatings Technology, 2011. 206(2): p. 542-552. 52. Chattopadhyay, A., et al., Studies on hot-rolled galvanized steel sheets: Segregation of alloying elements at the surface. Scripta Materialia, 2008. 59(5): p. 522-525. 53. Graat, P. and M.A. Somers, Quantitative analysis of overlapping XPS peaks by spectrum reconstruction: determination of the thickness and composition of thin iron oxide films. Surface and interface analysis, 1998. 26(11): p. 773-782. | |
dc.identifier.uri | http://tdr.lib.ntu.edu.tw/jspui/handle/123456789/51686 | - |
dc.description.abstract | 本論文主要針對22MnB5鋼板熱浸鍍鋅鍍層分成兩部分作探討,第一部分為鋅浴內鋁含量0.14wt%,第二部分為提高鋅浴內鋁含量至2.5wt%與10wt%,分別探討熱浸鍍鋅性質,鍍鋅後鍍層之高溫氧化性質與合金化之差異。第一部分研究,於450℃之鋅浴熱浸鍍3秒後,已可發現有一連續的δ相於介面處生成。此外,於500℃進行合金化處理0秒時,介面已生成Γ1相,且550℃合金化25秒後,XRD鑑定下得知,鍍層開始轉變成由Γ相為主的Fe-Zn相,顯示22MnB5鋼板於熱浸鍍鋅製程上,鍍層與鋼底材具有快速之交互反應。熱浸鍍鋅試樣經600℃及700℃預熱處理後,鍍層變得非常破碎,若當鍍層內的鐵含量較高,將使鍍層內鋅元素的蒸汽化速率小於氧化速率,此時鍍層傾向生成連續氧化皮膜,免於形成破碎的鍍層形貌。此外,在700℃的預熱處理5分鐘後,可在鍍層與鋼底材介面處生成厚度約5 μm之擴散層,爾後隨著時間增加,於30分鐘的預熱處理後,擴散層厚度可達約10 μm。然而,擴散層內的Zn含量於700℃的預熱處理下皆約為20 at%;600℃的預熱處理條件下,鍍層內的鋅含量則是逐漸增加至30分鐘的約12 at%左右。計算擴散層的成長機制,皆屬於體擴散之快速擴散機制。隨後,預熱處理過後的試片再經過950℃熱處理之後的鍍層皆產生約10 μm左右的氧化物,成分為ZnO與ZnFe2O4,直接950℃熱處理的試片氧化層較薄,成分為ZnO與ZnMn2O4,此兩種不同的氧化物皆為尖晶石結構,皆無法有效抵抗高溫氧化,而增加一預熱處理並無法改善鍍層的氧化行為,反而增加鍍層高溫氧化現象的發生,對提升抗氧化性質並無幫助。接著利用Gleeble進行高溫拉伸測試,模擬現場熱衝壓製程,可發現未經預熱處理者,具有提早破壞的現象,此現象即歸咎於液態金屬脆化的發生。
第二部分研究顯示鋅浴內較高的含鋁量將造成熱浸鍍實驗時無法全面鍍覆,以10wt%Al-Zn的鋅浴而言,需要提高鋅浴溫度至470℃才可避免裸露點的產生,鍍層結構與第一年相同皆為GI-純鋅相、GA-δ相,且發現高溫氧化性質與試片表面之元素分佈相關,若試片表面Al/(Zn+Fe)的數值越高,則抵抗高溫氧化的效果越佳,氧化物越薄,也利用短時間的預熱處理;如在550℃預熱25-50秒,能夠有效再提高表面Al/(Zn+Fe)的數值,使沃斯田鐵化後試片表面幾乎無氧化物覆蓋,鍍層結構亦轉變為單一相α-Fe(Zn)之結構,因此同時解決了熱浸鍍鋅鍍層應用在熱衝壓製程所遇到的兩大問題:高溫氧化與液態金屬脆化(Liquid metal induced embrittlement)。 | zh_TW |
dc.description.abstract | The research in this thesis was mainly about the high temperature oxidation behavior and alloy reaction of hot-dip galvanized 22MnB5 steel. The first part of the results and discussion was focused in low aluminum content in the zinc bath(0.14wt%). A continuous δ phase attains between coating and steel substrate after hot dip in 450℃ molten Zn bath for 3 s on 22MnB5 steel. Moreover, Γ1 phase shows up as the galvanized specimen was heated up to 500℃ and cooled down to room temperature immediately. The Γ phase, identified by the XRD, replaces the δ phase when galvannealed at 550℃ for longer than 25 s, implying that the 22MnB5 steels with faster interaction with coating. After the preheating treatment at 600℃ and 700℃, the coating layer became porous due to the vaporization of Zn, which broken the coating. As the Fe content in coating is higher, the coating tends to oxidation rather than vaporization. The period of preheating treatment at 700℃ to form a continuous diffusion layer is 5 min with thickness of 5um, while it took 30 min to form a continuous diffusion layer with thickness of 8um at 600℃. Moreover, the Zn content in diffusion layer is about 20 at.% for specimens after 700℃ preheat treatment. The results show that higher preheating treatment temperature results in higher Zn content and faster growth of diffusion layer. The specimens after preheating treatment was sent to austenize at 950℃ for 5min, main oxides were composed of zinc oxide and iron oxide, with a thicker oxide layer compared to those without preheating treatment before austenization. Hence, it can be concluded that a preheating treatment is useless for improving the high temperature oxidation resistance, but go through a preheating treatment can avoid liquid metal induced embrittlement by attain a single phase coating composed of α-Fe(Zn) due to the longer diffusion time. The aims of the second part of the results and discussion were the effect of higher aluminum content in the zinc bath on high temperature oxidation behavior and alloy reaction. The temperature of zinc bath was increased to 470℃ to avoid the bare spots after galvanizing due to the higher viscosity of Zn-Al alloy. The microstructure of hot-dip Zn-Al alloy was studied as well, composed of pure zinc for GI-specimen and δ phase for GA. Even for such a high aluminum content as 10wt%Al-Zn, the GA specimen was still covered by thicker oxides containing zinc and iron oxide after austenization at 950℃ for 5min. The XPS results show that the oxidation behavior would depends on the atomic ratio of Al/(Zn + Fe) around the surface of the coating. The preheating treatment of the first part of the research was conducted at 600℃ or 700℃ for a long time and the galvannealing process both increase the iron content in the coating, in other words, decrease the atomic ratio of Al/(Zn + Fe) around the surface of the coating. Hence, a preheating treatment at 550℃ for 25-50 seconds was chosen to increase the atomic ratio of Al/(Zn + Fe) on the top surface due to the high affinity between aluminum and oxygen, which, in turn, improves the high temperature oxidation resistance. | en |
dc.description.provenance | Made available in DSpace on 2021-06-15T13:44:34Z (GMT). No. of bitstreams: 1 ntu-104-R02527056-1.pdf: 9040918 bytes, checksum: 51d3f92f5aa5207c6d963e1da4bd4b64 (MD5) Previous issue date: 2015 | en |
dc.description.tableofcontents | 口試委員會審定書 i
致謝 ii 中文摘要 iii Abstract v 圖目錄 x 表目錄 xv 第一章 研究計畫之背景及目標 1 第二章 文獻搜尋與分析 4 2-1. 先進高強度鋼 4 2-1.1 先進高強度鋼之發展 4 2-1.2 麻田散鐵強化鋼 4 2-2. 熱浸鍍鋅 6 2-2.1 熱浸鍍鋅製程介紹 6 2-2.2 鐵鋅合金相結構與性質 7 2-2.3 彩色化學晶相腐蝕 8 2-3. 熱衝壓 9 2-3.1 應用於熱衝壓製程之鍍層 10 2-4. 氧化機構 13 2-4.1 金屬氧化反應機構 13 2-4.2 氧化熱力學 15 2-4.3 氧化動力學 17 2-4.4 Pilling-Bedworth ratio 19 2-4.5 提高鍍層抗高溫氧化能力 20 2-4.6 高溫熱處理對熱浸鍍鋅鍍層結構之影響 23 2-5. LMIE現象的改善 24 第三章 研究方法及研究步驟 26 3-1. 熱浸鍍鋅 26 3-2. 橫截面試樣製備 29 3-3. 彩色化學腐蝕金相 30 3-4. 掃描式電子顯微鏡觀察 (SEM) 30 3-5. 電子探測微分析儀 (EPMA) 31 3-6. X光繞射分析 (XRD) 31 3-7. 高解析X射線光電子能譜儀 (XPS) 32 3-8. 預熱處理 32 3-9. 熱衝壓製程 32 3-10. 高溫拉伸試驗 33 第四章 結果與討論 35 4-1. 熱浸鍍鋅 35 4-1.1 熱浸鍍鋅(鋅浴內含0.14wt%Al) 35 4-1.2 預熱處理 43 4-1.3 950℃沃斯田鐵化熱處理 51 4-1.4 950℃熱衝壓與高溫拉伸試驗 54 4-2. 熱鍍鋅鋁合金 58 4-2.1 熱鍍鋅鋁合金( 2.5wt%、10wt%Al-Zn ) 58 4-2.2 950℃沃斯田鐵化熱處理 64 4-2.3 預熱處理 77 4-2.4 高溫拉伸試驗 80 第五章 結論 83 參考文獻 86 | |
dc.language.iso | zh-TW | |
dc.title | 錳硼鋼鋼板熱浸鍍鋅鍍層高溫氧化行為與合金化之研究 | zh_TW |
dc.title | High temperature oxidation behavior and alloy reaction of hot-dip galvanized Mn-B steel | en |
dc.type | Thesis | |
dc.date.schoolyear | 104-1 | |
dc.description.degree | 碩士 | |
dc.contributor.oralexamcommittee | 王朝正,蔣龍仁 | |
dc.subject.keyword | 22MnB5鋼板,熱浸鍍鋅,合金化,高溫氧化,液態金屬脆化, | zh_TW |
dc.subject.keyword | 22MnB5,HDG,galvanized,oxidation,LMIE,XPS, | en |
dc.relation.page | 90 | |
dc.rights.note | 有償授權 | |
dc.date.accepted | 2015-12-04 | |
dc.contributor.author-college | 工學院 | zh_TW |
dc.contributor.author-dept | 材料科學與工程學研究所 | zh_TW |
顯示於系所單位: | 材料科學與工程學系 |
文件中的檔案:
檔案 | 大小 | 格式 | |
---|---|---|---|
ntu-104-1.pdf 目前未授權公開取用 | 8.83 MB | Adobe PDF |
系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。