請用此 Handle URI 來引用此文件:
http://tdr.lib.ntu.edu.tw/jspui/handle/123456789/15221
完整後設資料紀錄
DC 欄位 | 值 | 語言 |
---|---|---|
dc.contributor.advisor | 莊東漢(Tung-Han Chuang) | |
dc.contributor.author | Chun-Hao Chen | en |
dc.contributor.author | 陳俊豪 | zh_TW |
dc.date.accessioned | 2021-06-07T17:28:39Z | - |
dc.date.copyright | 2020-04-29 | |
dc.date.issued | 2018 | |
dc.date.submitted | 2020-04-15 | |
dc.identifier.citation | [1] Moore, Gordon E. (1965). 'Cramming more components onto integrated circuits'. Electronics Magazine. p. 4.
[2] Brock, David C., ed. (2006). Understanding Moore's law: four decades of innovation. Philadelphia, Pa: Chemical Heritage Press. ISBN 0941901416. [3] '1965 – 'Moore's Law' Predicts the Future of Integrated Circuits'. Computer History Museum. 2007. [4] User Wgsimon. (May 13, 2011). Microprocessor Transistor Counts 1971-2011 & Moore’s Law. Abstract retrieved from March 30, 2015, from http://en.wikipedia.org/wiki/Moore%27s_law#/media/File:Transistor_Count_and_Moore%27s_Law_-_2011.svg [5] D. Hisamoto, T. Kaga, and E. Takeda, Impact of the vertical SOI 'DELTA' structure on planar device technology, IEEE Transactions on Electron Devices, vol. 38 (6), pp. 1419–1424, June, 1991. doi:10.1109/16.81634. [6] D. Hisamoto et al., Impact of the vertical SOI 'Delta' Structure on Planar Device Technology, IEEE Transactions on Electron Devices, vol. 41 pp. 745, 1991. [7] C. Hu, J. Bokor, et al., FinFET-a self-aligned double-gate MOSFET scalable to 20 nm, IEEE Transactions on Electron Devices, vol. 47 (12), pp. 2320–2325, Dec. 2000. doi:10.1109/16.887014. [8] J. Cartwright, Intel enters the third dimension, Nature, May. 2011. [9] Intel to Present on 22-nm Tri-gate Technology at VLSI Symposium (ElectroIQ 2012) Archived April 15, 2012, at the Wayback Machine. [10] C. A. Giffels, R J. Gashler, J. M. Morabito and K. M. Striny, “Interconnection Media”, AT&T Technical Journal, Vol. 66, No. 4 (1987) pp. 31-44. [11] M. R. Pinnel and W. H. Knausenberger, “Interconnection System Requirements and Modeling”, AT&T Technical Journal, Vol. 66, No. 4, pp. 45-56, 1987. [12] Electronic Packaging:Solder Mounting Technologies in K.H. Buschow et al (ed), Encyclopedia of Materials:Science and Technology, Elsevier, ISBN 0-08-043152-6, pp. 2708-2709, 2001. [13] P. Horowitz, W. Hill, The art of electronics (2nd ed.). Cambridge, Cambridge Univ. Press. ISBN 9780521370950, 1989. [14] C. Taube (Dec. 29, 2006). A MOS 6581 sound chip from a Commodore 64 main board. Abstract retrieved from May 04, 2017, from https://upload.wikimedia.org/wikipedia/commons/0/0f/MOS6581_chtaube061229.jpg [15] J. Fader (Dec. 07, 2004). Surface-mount components on a USB flash drive's circuit board. Abstract retrieved from May 04, 2017, from https://commons.wikimedia.org/wiki/File:Smt_closeup.jpg [16] H. W. Hsueh et. al., Intermetallic Phase on the Interface of Ag-Au-Pd/Al Structure, Advances in Materials Science and Engineering, pp. 6, 2014. [17] T. C. Wei, and A. R. Daud, Mechanical and Electrical Properties of Au-Al and Cu-Al Intermetallics Layer at Wire Bonding Interface, Journal of Electronic Packaging, vol. 125(4), pp. 617-620, 2003. [18] G. Harman, and J. Albers, The Ultrasoniuc Welding Mechanism as Applied to Aluminum and Gold-Wire Bonding, Microelectronics. Parts, Hybrids, and Packaging, IEEE Transactions, vol. 13(4), pp. 406-412., 1977. [19] H. Okamoto, Al-Au (Aluminum-Gold), Journal of Phase Equilibria and Diffusion, Vol. 26 No. 4, pp. 391-393, 2005. [20] D. Haase, Gold-Bärenmarkt erst 2016 beendet?, 31th, Jan. 2014, Abstract retrieved from May 17, 2017, from http://www.goldseitenblog.com/daniel_haase/index.php/2014/01/31/gold-baerenmarkt-erst-2016-beendet [21] J. D. Lee, H. H. Tsai, T. H. Chuang, Alloy wire and methods for manufacturing the same, US Patent 8,940,403 B2, 2015. [22] H. H. Tsai, J. D. Lee, C. H. Tsai, H. C. Wang, C. C. Chang, and T. H. Chuang, An innovative annealing-twinned Ag-Au-Pd bonding wire for IC and LED packaging, Proc. Int. Microsystem Packaging Assembly and Circuit Technology Conf., IMPACT, Taipei, pp. 505-508, 2012. [23] S. C. Wang, Electromigration and Annealing Grain Structure of Ag-alloy Wires for Electronic Packaging, National Taiwan University, Institute of Materials Science and Engineering, 2013. [24] H. J. Lin, Thermal Stability and Electromigration Durability of Annealing Twinned Ag-Pd Alloy Wires, National Taiwan University, Institute of Materials Science and Engineering, 2016. [25] Y. C. Lin, Material Characteristic of Electronic Packaging Ag-alloy Bonding Wires under Current Stressing, National Taiwan University, Institute of Materials Science and Engineering, 2017. [26] O. L. Anderson, H. Christensen, P. Andreatch, Technique for Connecting Electrical Leads to Semiconductors, Journal of Applied Physics, vol. 28, pp. 923, 1957. [27] Hshekhani (June 03, 2016). Ball and bond formation. Abstract retrieved from Dec. 19, 2017, from https://upload.wikimedia.org/wikipedia/commons/5/5a/Ball_bondpt1.png [28] J. H. Cho et. al., Recrystallization and grain growth of cold-drawn gold bonding wire, Metallurgical and Materials Transactions A, vol. 34(5), pp. 1113-1125, 2003. [29] H. Lichtenberger, G. Toea, and M. Zasowski, Development of low loop. Long length, hydrostatically extruded bonding wire, Advanced Packaging Materials, Proceedings., 3rd International Symposium, 1997. [30] B. Marz, A. Graff, R. Klengel, and M. Petzold, “Interface microstructure effects in Au thermosonic ball bonding contacts by high reliability wire materials,” Microelectronics Reliability, vol. 54, 2014, pp. 2000-2005. [31] P. Ratchev, S. Stoukatch, and B. Swinnen, Mechanical reliability of Au and Cu wire bonds to Al, Ni/Au and Ni/Pd/Au capped Cu bond pads, Microelectronics Reliability, vol. 46, pp. 1315-1325, 2006. [32] H. Xu et. al., Intermetallic phase transformations in Au-Al wire bonds, Intermetallics, vol. 19, pp. 1808-1816, 2011. [33] H. J. Kim, J. S. Cho, Y. J. Park, J. Lee, and K. W. Paik, Effects of Pd Addition on Au stud Bumps/Al Pads Interfacial Reactions and Bond Reliability, Journal of Electronic Materials, vol. 33, pp. 1210-1218, 2004. [34] H. Xu et. al., A re-examination of the mechanism of thermosonic copper ball bonding on aluminum metallization pads, Scripta Materialia, vol. 61, pp. 165-168, 2009. [35] A. Shah et. al, In situ ultrasonic force signals during low-temperature thermosonic copper wire bonding, Microelectronic Engineering, vol. 85, pp. 1851-1857, 2008. [36] B. K. Appelt et. al., Fine pitch copper wire bonding in high volume production, Microelectronics Reliability, vol. 51, pp. 13-20, 2011. [37] B. In-Tae, J. Dae Young, and D. Yong, Electron microscopy study on intermetallic compound formation in Cu-Al bond interface, Electronic Components and Technology Conference (ECTC), 2012. [38] H. J. Kim, J. Y. Lee, K. W. Paik, K. W. Koh, J. Won, S. Choe, J. Lee, J. T. Moon, and Y. J. Park, Effects of Cu/Al intermetallic compound (IMC) on copper wire and aluminum pad bondability, IEEE Trans. Compon. Packag. Manuf. Technol., vol. 26, no. 2, pp. 367-374, Jun. 2003. [39] Semitracks, INC., Scanning Electron Microscope, Retrieved from https://www.semitracks.com/reference-material/failure-and-yield-analysis/failure-analysis-die-level/scanning-electron-microscope.php [40] Small Precision Tools, Copper Wire Bonding Process, Retrieved December 25, 2017, from http://www.smallprecisiontools.com/products-and-solutions/chip-bonding-tools/bonding-capillaries/technical-guide/basics-of-ball-bonding-process/copper-wire-bonding-process/?oid=1260&lang=en [41] A. Pequegnat, H. J. Kim, M. Mayer, Y. Zhou, J. Persic, J. T. Moon, Effect of gas type and flow rate on Cu free air ball formation in thermosonic wire bonding, Microelectronic Reliability, vol. 51, pp. 43-52, 2011. [42] C. J. Hang, C. Q. Wang, M. Mayer, Y. H. Tian, Y. Zhou, H. H. Wang, Growth behavior of Cu/Al intermetallic compounds and cracks in copper ball bonds during isothermal aging, Microelectronic Reliability, vol. 48, pp. 416-424, 2008. [43] P. Chauhan, Z. W. Zhong, and M. Pecht, Copper wire bodning concerns and best practices, J. Electronic. Mater., vol. 42, no. 8, pp. 2415-2434, 2013. [44] S. Schmitz, M. Schneider-Ramelow, S. Schroder, Influence of bonding process parameters on chip cratering and phase formation of Cu ball bonds on AlSiCu during storage at 200℃, Microelectronics Reliability, vol. 51, pp. 107-112, 2011. [45] T. Uno, and T. Yamada, Improving humidity bond reliability of copper bonding wires, Electronic Components and Technology Conference (ECTC), Proceedings 60th, 2010. [46] D. Stephan et. al., Impact of palladium to the interfacial behavior of palladium coated copper wire on aluminum pad metallization during high temperature storage, Electronics Packaging and Technology Conference (EPTC), IEEE 13th, 2011. [47] M. N. M. Ching, K. J. Lee, Influence of Nitrogen and Forming Gas towards Palladium Coated Copper Wire, Electronics Packaging and Technology Conference (EPTC), IEEE 13th, 2011. [48] A. B. Y. Lim, A. C. K. Chang, O. Yauw, B. Chylak, C. L. Gan, Z. Chen, Ultra-fine pitch palladium-coated copper wire bonding: Effect of bonding parameters, Microelectronics Reliability, vol. 54, pp. 2555-2563, 2014. [49] N. A. Zarkevich, and D. D. Johnson, Predicted hcp Ag-Al metastable phase diagram, equilibrium ground states, and precipitate structure, Physical Review B, 67, pp. 064104, 2003. [50] M. R. Choi, H. G. Kim, T. W. Lee et.al., Microstructural evaluation and failure analysis of Ag wire bonded to Al pads, Microelectronics Reliability, vol. 55, pp. 2306-2315, 2015 [51] M. Schneider-Ramelow et. al., Development and Status of Cu Ball/Wedge Bonding in 2012, Journal of Electronic Materials, vol. 42, pp. 558-595, 2013. [52] K. A. Yoo et al., Reliability Study of Low Cost Alternative Ag Bonding Wire with Various Bond Pad Materials, 11th Electronic Packaging Technology Conference (EPTC), Singapore, pp. 851-857, Dec. 2009. [53] T. K. Chang, Gold wire for use in semiconductor packagimg and high-frequency signal transmission, US patent 6,696,756 B2, 2004. [54] J. R. Black, Electromigration - A Brief Survey and Some Recent Results, IEEE Trans. on Electron Devices, Vol. ED-16 (No. 4), pp. 338-347, Apr. 1969. [55] S. A. Gam et. al., Effects of Cu and Pd addition on Au bonding wire/Al pad interfacial reactions and bond reliability, Journal of Electronic Materials, vol. 35, pp. 2048-2055, 2006. [56] H. H. Tsai et. al., High performance Ag-Pd alloy wires for high frequency IC packages, Microsystems, Packaging, Assembly and Circuits Technology Conference (IMPACT), 8th International, pp. 162-165, 2013. [57] C. C. Chang, Interfacial reactions of Ag alloy wires with wire bonded pads for IC and LED packages, in National Taiwan University, Institute of Material Science and Engineering, 2013. [58] M. A. Tschopp, S. P. Coleman, and D. L. McDowell, Symmetric and asymmetric tilt grain boundary structure and energy in Cu and Al (and transferability to other fcc metals), Integrating Materials and Manufacturing Innovation, pp. 4-11, 2015. [59] Y. Z. He, Effect of Pd Content on Ion Migration of Ag-alloy Bonding Wires, National Taiwan University, Institute of Materials Science and Engineering, 2016. [60] T. H. Chuang, C. C. Chang, C. H. Chuang, J. D. Lee and H. H. Tsai, Formation and growth of intermetallics in an annealing-twinned Ag-8Au-3Pd wire bonding package during reliability tests, IEEE Transactions of Component, Packaging and Manufacturing Technology, vol. 3, no. 1, pp. 3-9, 2013. [61] H. Foell, Defects in Crystals, University of Kiel, Faculty of Engineering, Abstract retrieved from July 17, 2018, from https://tf.uni-kiel.de/matwis/amat/def_en/kap_7/backbone/r7_1_1.html [62] S. Mahajan et. al., Formation of annealing twins in f.c.c. crystals, Acta Materia, vol. 45, pp. 2633-2638, 1997. [63] I. L. Dillamore, A determination of the stacking-fault energy of some pure F.C.C. metals, Philosophical Magazine, 9(99), pp. 517-526, 1964 [64] L. E. Murr, Interfacial Phenomena in Metals and Alloys, Addison Wesley, 1975. [65] K. J. Puttlitz, K.A. Statler, Handbook of Lead-Free Solder Technology for Microelectronic Assemblies, CRC Press, 2004. [66] K. E. Schwarz, Elektrolytische Wanderung in flüssigen und festen Metallen, vol. 46, Issue 3, pp. 247, Leipzig 1940. [67] W. Seith, Diffusion in Metallen, 1st edition, 1939. [68] V. B. Fiks, On the mechanism of the mobility of ions in metals, Soviet Phys.-Solid State, vol. 1, pp. 14, 1959. [69] H. Wever, Uberfuhrungsversuche an festem kupfer, Electrochem., vol. 60, pp. 1170, 1956. [70] I. A. Blech et. al., RADC Tech. Rept. TR 66-31, December 1965. [71] I. A. Blech and E. S. Meieran, Electromigration in Thin Al Films, Journal of Applied Physics, vol. 40, pp. 485, 1969. [72] J. R. Black, Electromigration - A Brief Survey and Some Recent Results, IEEE Trans. on Electron Devices, Vol. ED-16 (No. 4), pp. 338-347, April 1969. [73] K. Kyung-Hoae, Comparison study of future on-chip interconnects for high performance VLSI applications,' Ph.D. dissertation, Dept. Elect. Eng., Stanford Univ., Stanford, CA, USA, Mar. 2011. [74] H. B. Huntington, and A. R. Grone, Current-induced marker motion in gold wire, J. Phys. Chem. Solids, vol. 20(1-2), pp. 76-87, 1961. [75] F. M. d’Heurle, “Electromigration and failure in electronics: An introduction,” Proc. IEEE, vol. 59, pp. 1409–1418, Oct. 1971. [76] M. Shatzkes and J. R. Lloyd, “A model for conductor failure considering diffusion concurrently with electromigration resulting in a current exponent of 2,” J. Appl. Phys., vol. 59, pp. 3890–3893, June 1, 1986. [77] J. Schoonman, The ionic conductivity of pure and doped lead bromide single crystals, Journal of Solid State Chemistry, vol. 4, pp. 466-474, 1972. [78] R. E. Hoffman and D. Turnbull: J. Appl. Phys., 1951, vol. 22, no. 5, pp. 634-639. [79] N. I. Papanicolaou, G.A. Evangelakis, and G.C. Kallinteris: Comput. Mater. Sci., 1998, vol. 10, pp. 105-110. [80] T. H. Chuang, H. J. Lin, H.C Wang, C. H. Chuang, and C. H. Tsai, Mechanism of electromigration in Ag-alloy bonding wires with Different Pd and Au content, Journal of Electronic Materails, vol. 44, no. 2, pp. 623-629, 2015. [81] B. Stahlmecke, F. J. Meyer zu Heringdorf, L. I. Chelaru, M. Horn-von Hoegen, and G. Dumpich, Electromigration in self-organized single-crystalline silver nanowires, Applied Physics Letters, vol. 88, pp. 053122, 2006. [82] H. W. Hsueh, F. Y. Hung, T. S. Lui and L. H. Chen, Effect of the direct current on microstructure, tensile property and bonding strength of pure silver wires, Microelectronics Reliability, vol. 53, pp. 1159-1163, 2013. [83] H. W. Hsueh, F. Y. Hung, and T. S. Lui, A study on electromigration-inducing intergranular fracture of fine silver alloy wires, Applied Physics Letters, vol. 110, pp. 031902, 2017. [84] R. E. Hummel and H. J. Geier, Thin Solid Films, 1975, vol. 25, no. 2, pp. 335-342. [85] A Chatterjee, T. Bai, F. Edler, C. Tegenkamp, K. Weide-Zaage and H. Pfnür, J. Phys.: Condens. Matter., vol. 30, pp. 084002, 2018. [86] K. C. Chen, W. W. Wu, C. N. Liao, L. J. Chen, K. N. Tu, Observation of Atomic Diffusion at Twin-Modified Grain Boundaries in Copper, Science, vol. 321, pp. 1066-1069, 2008 [87] H. P. Chen, C. W. Huang, C. W. Wang, W. W. Wu, C. N. Liao, L. J. Chen and K. N. Tu, Optimization of the nanotwin-induced zigzag surface of copper by electromigration, Nanoscale, vol. 8, pp. 2584-2588, 2016. [88] J. Cho and C. V. Thompson. Grain Size Dependence of Electromigration-Induced Failures in Narrow Interconnects, Applied Physics Letters, vol. 54, pp. 2577, 1989. [89] V. T. Srikar, Electromigration Behavior and Reliability of Bamboo Al(Cu) Interconnects for Integrated Circuits, MASSACHUSETTS INSTITUTE OF TECHNOLOGY , Department of Materials Science and Engineering, 1999. [90] John E. Sanchez, L. T. McKnelly, and J. W. Morris, Slit morphology of electromigration induced open circuit failures in fine line conductors, Journal of Applied Physics, vol. 72, pp. 3201-3203, 1992. doi: 10.1063/1.351484 [91] A. Magnaterra, Structure factor and resistivity of copper and silver, Physics Letters, vol. 44A, no. 1, pp. 63-64, 1973. [92] R. Guo, L. Gao, M. Li, D. Mao, K. Qian, and H. Chiu, Microstructure evolution of Ag–8Au–3Pd alloy wire during electromigration, Materials Characterization, vol. 110, pp. 44-51, 2015. [93] C. M. Li, P. Yang, D. M. Liu, N. C. Hung, and M. Li, A Preliminary Electron Backscatter Diffraction Study of Microstructures and Microtextures Evolution during Au Stud and Flip Chip Thermosonic Bonding, Journal of ELECTRONIC MATERIALS, Vol. 36, No. 5, pp. 587-592, 2007. [94] F. Wulff, C. D. Breach, and K. Dittmer, Crystallographic texture of drawn gold bonding wires using electron backscattered diffraction (EBSD), J. Mater. Sci. Lett., Vol. 22, pp. 1373, 2003. [95] S. M. Baeck, K. K. Park, H. Ha, Y. Oh, Y. Park, J. T. Moon, J. Lee, and K. H. Oh, Texture Analysis of Copper Bonding Wire, Mater. Sci. Forum, vol.803, pp. 408–412, 2002. [96] F. Brisset, A.-L. Helbert, and T. Baudin, In Situ Electron Backscatter Diffraction Investigation of Recrystallization in a Copper Wire, Microscopy and Microanalysis, pp. 1-9, 2013. doi:10.1017/S1431927613000299 [97] T. Boellinghaus, V. Lüders, and G. Nolze, Microstructural Insights into Natural Silver Wires, Scientific Reports, vol. 8, pp. 9053, 2018. [98] Z. Ren, Silver Bonding Wire for BSOB(Bond-Stitch-on-Ball)/BBOS(Bonding-Ball-on-Stitch), China Semiconductor Technology International Conference (CSTIC), 2016. [99] Orientation Imaging Microscopy (OIM) Analysis, Abstract retrieved from July 17, 2018, from https://edax.com/products/ebsd/oim-analysis [100] B. R. Coles, Electronic Structures and Physical Properties in the Alloy Systems Nickel-Copper and Palladium-Silver, Proc. Phys. Soc. B, vol. 65, pp. 221-229, 1952. [101] René de Kloe, “DO YOU WANT TO BE AVERAGE?”, EDAX AMETEK, Abstract retrieved from July 17, 2018, from https://edaxblog.com/do-you-want-to-be-average-%E4%BD%A0%E6%83%B3%E8%A2%AB%E5%B9%B3%E5%9D%87%E5%90%97/ [102] F. C. Campbell: Elements of Metallurgy and Engineering Alloys, 1st ed., ASM International, United States of America, 2008, pp. 265-276. | |
dc.identifier.uri | http://tdr.lib.ntu.edu.tw/jspui/handle/123456789/15221 | - |
dc.description.abstract | 電子封裝製程技術的進步,促使消費性電子產品達成短小與輕薄化的要求,然而便攜性帶來的可靠度影響實為一不容忽視之問題,近年來電子產業開始使用銀合金線做為金線替代材,然而高頻通訊與電動車模組的高電流密度常態使用,加劇導線發生廣為人知的電遷移現象;有鑑於此,本研究第一部份即針對銀合金銲線探討電遷移現象與機制,基於此項研究經驗,發展針對銀合金帶材與線材的電子背向散射繞射分析技術,並透過此技術從另一面向究明銀合金帶材與線材的退火與電遷移過程的材料特性與晶粒結構。
為求電遷移實驗線材實際溫度準確性,本研究第一部分之電遷移實驗採用本實驗室自行研發之耐高溫夾具,對線徑17.6 μm的四種不同鈀含量之銀鈀合金線,於高溫環境下進行電遷移,結果顯示添加量2~6 wt.% Pd之銀鈀合金線,電遷移活化能為0.36~0.46 eV,為表面擴散路徑主導。為徹底了解Ag-4Pd銀合金線線材結構成因,本研究第二部分進行銀合金帶材輥軋退火研究,並以創新的電子背向散射繞射技術對Ag-4Pd銀合金線內部晶格結構做一全面的了解;結果顯示,Ag-4Pd銀合金帶材經退火後晶粒大小與孿晶晶界佔比和退火溫度高低較相關,而與退火時間長短較無關聯。晶粒大小成長與孿晶密度佔比都與退火溫度呈現線性趨勢增加,其晶粒成長活化能為0.47 eV,與第一部分Ag-4Pd線材活化能接近,並且,多道次輥軋能有效增加Ag-4Pd帶材內部孿晶晶界佔比,並由KAM圖得知銀合金退火前後殘留應力釋放與晶粒成型相關性。 本研究第三部分針對17.6 μm的Ag-4Pd銀合金線,以電子背向散射繞射技術對銀合金線的電遷移過程特性做分析;本實驗室基於帶材經驗,發展出一套特殊的線材EBSD試片製備技術,成功突破銀合金線材EBSD試片製備瓶頸,為世界首創關於線材電遷移過程特性的EBSD研究。透過電子背向散射繞射技術分析線材結構,可以得知線材中心部分長條晶結構的晶格取向為<100>,線材外圍部分則是無序、富含退火孿晶的細晶粒,並透過與KAM圖與帶材結果對照可知,中心長條晶成因實為冷加工抽線殘留織造(texture),外圍則是經線材退火製程而再結晶成長之晶粒。後續設計室溫(25 oC)與高溫(150 oC)線材電遷移實驗,取各時間段線材進行EBSD分析,結果顯示線材通電後,內部晶粒快速成長,原始線材晶界電遷移後絕大多數快速地轉為Σ3或是Σ9的孿晶晶界與垂直電子流方向的竹節狀晶界,並在總體孿晶晶界密度達到約80 %後停止,此結果與孿晶晶界的低自由能特性有關,並受溫度影響在高溫環境加速進行。透過EBSD分析各時間段下線材結構與晶格取向,可推論銀合金電遷移破壞機制分為三階段:1)初期晶界快速轉化為孿晶與竹節狀晶界;2)中期線材內部結構穩定後轉為表面電遷移效應;3)線材表面形貌改變,線徑減縮區域使電流密度加大而燒斷。 | zh_TW |
dc.description.abstract | The flourish improvements of electronic packaging technology allows the developing trend of electronic devices to be light-weight, gaunt and neat. However, reliability issues such as electromigration caused by relatively high current density usage inside high-frequency components and power modules also arises. Hence, in order to establish a comprehensive understanding of Ag-alloy wire property and failure mechanism, our research focus on the complete study of electromigration phenomenon and the wire structure itself.
Firstly, the failure mechanism of Ag-Pd bonding wire has been investigated by stressing with 1.23 x 105 A/cm2 current density at 150 ~ 300 oC. The results showed that the activation energy of Ag-Pd bonding wires to be 0.36 ~ 0.46 eV as the doping content of Pd arises from 2 to 6 wt.%. On the other hand, grain structures and surface morphologies of Ag-4Pd bonding wires were investigated after electromigration, indicating surface diffusion to be the dominant mechanism during electromigration for Ag-4Pd bonding wire. Secondly, in order to clarify the characteristic and grain structure of Ag-4Pd Ribbon, an innovative Electron Back Scatter Diffraction analysis for Ag-4Pd ribbon was proposed. By applying EBSD technique, characterization of twin boundary and average grain size were investigated during the annealing treatment of Ag-4Pd ribbon. The result showed that twin boundary densities increased originally from 3.7 % up to 77 % as the annealing temperature arose, and the average grain size were also grew from 0.28 μm to 8.46 μm with elevating annealing temperature. The grain growth activation energy was calculated to be 0.47 eV which is quite near to the activation energy of electromigration. Our study also found that after long time treatment there was not significant difference among twin boundary densities(60~70%) and grain structure(1.20 μm) of Ag-4Pd ribbon itself, whereas staged rolling and annealing can increase the twin boundary densities up to 70% above. Last, the mechanism and grain structure of electromigration of Ag-4Pd was investigated. In present study, the grain structure of Ag-4Pd bonding wire was characterized by EBSD analysis, and the microstructure of grain evaluation during electromigration were recorded. Regions in the centre of Ag-4Pd bonding wire was characterized to be <100> orientation, and they are reckoned as the inheritance of the cold-draw texture during wire manufacturing procedure. Twin boundary densities arose from 25.5 % to about 80 % after electromigration. The evolution of the increasing twin boundary densities during electromigration can be attributed by relatively lower grain boundary energy of CSL boundary and the resistance against electromigration. Hence, the failure mechanism of Ag-4Pd bonding wire can be classified into three stages: 1)Initial Stage: grain boundary migration; 2)Secondary stage: Termination of grain boundary migration, surface diffusion dominates; 3)Failure stage: failure occurs due to the local shrinkage of wire diameter. | en |
dc.description.provenance | Made available in DSpace on 2021-06-07T17:28:39Z (GMT). No. of bitstreams: 1 ntu-107-D04527008-1.pdf: 22600120 bytes, checksum: 90e93c88aa3080c7a32dde975f86863f (MD5) Previous issue date: 2018 | en |
dc.description.tableofcontents | 目錄
口試委員審定書 # 誌謝 I 中文摘要 III Abstract V 目錄 VII 圖目錄 IX 表目錄 XIV 第一章 緒論 1 1-1 前言 1 1-2 研究動機 8 1-3 研究目的 10 第二章 文獻回顧 14 2-1 打線接合(Wire Bonding) 14 2-1-1 金線 21 2-1-2 銅線 24 2-1-3 純銀線與銀合金線 30 2-2 孿晶 35 2-3 電遷移(Electromigration)與其效應 39 2-3-1 電遷移模型與機制 41 2-3-2 合金銲線電遷移型態機制與微觀結構對電遷移之影響 45 2-4 電子背向散射技術(Electron Back-Scatter Diffration)與合金銲線分析 55 第三章 實驗方法 58 3-1 實驗流程圖 59 3-2 線材使用 60 3-3 實驗設備 60 3-3-1 電遷移實驗設備 60 3-3-2 電子背向散射試片製作與分析設備 64 3-4 分析方法 67 3-4-1 電遷移活化能 67 3-4-2 晶粒成長活化能 68 第四章 結果與討論 69 4-1 銀合金銲線之高溫電遷移實驗研究 69 4-1-1 Pd摻雜量變化對銀合金線材結構影響與電遷移行為 69 4-1-2 Ag-4Pd銀合金銲線高溫電遷移行為與擴散機制驗證 74 4-2 退火處理Ag-4Pd銀合金帶材Ribbon之材料特性與晶粒結構研究 83 4-2-1退火處理Ag-4Pd銀合金帶材Ribbon之晶粒結構與材料特性 83 4-2-2 Ag-4Pd銀合金帶材之電子背向散射分析技術(EBSD) 87 4-2-3 Ag-4Pd銀合金帶材長時間退火與多道次輥壓退火研究 98 4-3 Ag-4Pd銀合金銲線電遷移機制與結構分析研究 103 4-3-1 Ag-4Pd銀合金銲線材料結構分析 103 4-3-2 Ag-4Pd銀合金銲線電遷移過程材料特性分析 107 第五章 結論 118 參考文獻 119 | |
dc.language.iso | zh-TW | |
dc.title | 電子封裝Ag-4Pd銀合金銲線之退火處理及電遷移材料特性與晶粒結構研究 | zh_TW |
dc.title | Material Characteristics and Grain Structure of Electronic Packaging Ag-4Pd Bonding Wire under Electromigration and Annealing Treatment | en |
dc.type | Thesis | |
dc.date.schoolyear | 108-2 | |
dc.description.degree | 博士 | |
dc.contributor.oralexamcommittee | 施漢章,方立志,吳春森,張錦泉,蔡幸樺 | |
dc.subject.keyword | 銀合金線,活化能,電遷移,電子背向散射繞射分析,孿晶晶界密度, | zh_TW |
dc.subject.keyword | Ag-alloy bonding wire,electromigration,activation energy,electron back scatter diffraction,twin boundary, | en |
dc.relation.page | 130 | |
dc.identifier.doi | 10.6342/NTU202000749 | |
dc.rights.note | 未授權 | |
dc.date.accepted | 2020-04-16 | |
dc.contributor.author-college | 工學院 | zh_TW |
dc.contributor.author-dept | 材料科學與工程學研究所 | zh_TW |
顯示於系所單位: | 材料科學與工程學系 |
文件中的檔案:
檔案 | 大小 | 格式 | |
---|---|---|---|
ntu-107-1.pdf 目前未授權公開取用 | 22.07 MB | Adobe PDF |
系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。