標題: | 介質研磨對纖維素之酵素水解動力學的影響 Effect of Medium Milling on Kinetics of Enzymatic Hydrolysis of Cellulose |
作者: | Yi-Ching Huang 黃宜瑾 |
指導教授: | 葉安義 |
關鍵字: | 纖維素,酵素,水解,介質研磨,動力學, cellulose, enzymatic hydrolysis, medium milling, kinetics, |
出版年 : | 2007 |
學位: | 碩士 |
摘要: | 纖維素為地球上存量最多的多醣類,廣泛應用在食品、紙及能源等方面,具有極高的經濟價值。近年來,將纖維素降解成最小單位-葡萄糖,再進而醱酵成乙醇成為生質能為一熱門話題。本研究主旨為探討介質研磨對酵素水解纖維素的影響。實驗原料為高結晶的棉花纖維,體積平均粒徑為25.52 μm,經介質研磨後,體積平均粒徑下降至1 ~ 10 μm的範圍。利用不同纖維素濃度和研磨時間,製備不同平均粒徑之纖維素,再進行酵素水解反應,藉由葡萄糖(glucose)和纖維二糖(cellobiose)生成量的動力學模式,探討介質研磨對水解反應的影響。
將15 g、35 g纖維素原料與500 mL去離子水(即濃度3 %及7 %),以0.3 mm的釔鋯珠作為介質,研磨0、15、60、120分鐘後,3 %纖維素研磨濃度的體積平均粒徑分別為25.52 μm、5.54 μm、0.85 μm、0.78 μm,結晶度指數分別為94.4 %、87.5 %、74.3 %、77.0 %;7 %纖維素研磨濃度的體積平均粒徑分別為25.52 μm、6.08 μm、2.66 μm、2.07 μm,結晶度指數分別為94.4 %、87.6 %、76.0 %、86.5 %。經介質研磨後之纖維素加入來自里氏木黴(T. reesei) 之纖維素酶20 mg於40˚C 100 mL的醋酸鈉緩衝溶液中進行水解。結果顯示,動力常數Km與纖維素平均粒徑及結晶度呈正相關,水解速率、Vmax與纖維素平均粒徑及結晶度呈負相關,抑制常數Ki則無明顯趨勢。經研磨後平均粒徑0.78 μm之纖維素,Vmax由0.076 g/L-min提高至0.304 g/L-min,Km由9.844 g/L下降為1.877 g/L,Ki則由0.034 g/L變為0.016 g/L;在E/S (Enzyme/Substrate) = 0.08、120 ~ 200小時水解後,葡萄糖最終產率由50 %上升至90 %。觀察24小時內的水解,葡萄糖產率隨纖維素平均粒徑及結晶度下降而上升,葡萄糖產率自14.22 %提高約3倍至45.83 %。經120分鐘研磨的纖維素,只需1/4酵素量,即達到未研磨纖維素的葡萄糖產率。 Cellulose is the most abundant polysaccharide on the earth and is generally applied to foods, fuel, biomaterials and energy. Degradation of cellulose to glucose, which is then fermented to ethanol, is one of the hottest issues in the past decade. The objective of this study is to investigate the effect of medium milling on the kinetics of enzymatic cellulose hydrolysis. The volume average particle size of raw cellulose was reduced from 25.52 μm to 1 ~ 10 μm. Different concentration of cellulose and milling time produced cellulose with various average particle sizes for further enzymatic hydrolysis. Kinetics of glucose and cellobiose production was applied to explore the effect of milling on cellulose hydrolysis. 15 g or 30 g cellulose and 500 mL deionized water (i.e. 3 % or 7 %) were milled by milling medium, YTZ (yttria-stabilized tetragonal zirconia) beads with average diameter 0.3 mm. After 0, 15, 60 and 120 min milling, volume average particle size of 3 % cellulose was 25.52 μm, 5.54 μm, 0.85 μm and 0.78 μm, respectively, and crystallinity index was 94.4 %, 87.5 %, 74.3 % and 77.0 %, respectively; while for 7 % cellulose, volume average particle size was 25.52 μm, 6.08 μm, 2.66 μm and 2.07 |
URI: | http://tdr.lib.ntu.edu.tw/jspui/handle/123456789/30847 |
全文授權: | 有償授權 |
顯示於系所單位: | 食品科技研究所 |
文件中的檔案:
檔案 | 大小 | 格式 | |
---|---|---|---|
ntu-96-1.pdf 目前未授權公開取用 | 3.91 MB | Adobe PDF |
系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。