標題: | 大氣電漿沉積二氧化矽薄膜阻燃應用 Flame Retardant of Silicon Dioxide Film Deposited by Atmospheric Pressure Plasma Chemical Vapor Deposition |
作者: | Ming-Wei Liao 廖銘瑋 |
指導教授: | 張所鋐(Shuo-Hung Chang) |
關鍵字: | 大氣電漿,二氧化矽薄膜,阻燃,孔洞性,最低限氧指數, Atmospheric pressure plasma,SiO2,porosity,flame retardant,limiting oxygen index, |
出版年 : | 2008 |
學位: | 碩士 |
摘要: | 本文係利用噴射式大氣電漿鍍膜技術,將二氧化矽薄膜沉積在高分子材料聚碳酸酯(Polycarbonate,PC)表面,並探討不同特性的二氧化矽薄膜對阻燃性質提升的影響。電漿氣體為氦氣並在電源以射頻(Radio Frequency, RF)13.56 MHz來驅動電漿源。使用有機矽源的四乙氧基矽烷(tetraethoxysilane,TEOS)當作沉積二氧化矽薄膜的前驅物。改變不同的前驅物流量、功率大小及氧氣流量等實驗因子,來掌握二氧化矽薄膜的特性,了解薄膜孔洞性的變化。使用霍氏轉換紅外光譜儀(FTIR)、原子力顯微鏡(AFM)及掃描型電子顯微鏡(SEM)來分析二氧化矽薄膜的特性,同時以最低限氧指數(limiting oxygen index, LOI)的量測做為探討阻燃性的依據。
經大氣電漿所沉積的二氧化矽薄膜其孔洞性會受到成膜速率的影響,實驗結果發現二氧化矽薄膜的孔洞性隨著成膜速率的上升而增加,因此欲沉積緻密性較高的薄膜,應選擇成膜速率較低的參數。從最低限氧指數的量測發現,原本未沉積二氧化矽薄膜的最低限氧指數為22,鍍上孔洞性低的薄膜,可提升最低限氧指數至27,而相對地,孔洞性高的薄膜,對於阻燃性質的提升並無改善的現象。 Atmospheric pressure (AP) plasma chemical vapor deposition (CVD) process is utilized in this paper. We coated silica films on polycarbonate (PC) to enhance the flame retardant of PC. The AP apparatus is developed by ITRI. The plasma reactor operates by feeding helium gas between two electrodes driven by a Radio frequency (RF) power at 13.56 MHz at atmospheric pressure and near room temperature. The organic silicon source tetraethoxysilane (TEOS) was utilized as the precursor of silica films. With distinct experiment factors, such as the flow rate of precursor, power and flow rate of oxygen, we measure the thickness to calculate deposition rate, surface roughness, and porosity of the film. Moreover, the variation of the film’s properties were analyzed by Fourier-transform infrared spectrometer (FTIR), atomic force microscope (AFM) and scanning electron microscopy (SEM). The promotion of PC’s flame retardant is illustrated by limiting oxygen index. The result presented the porosity of the silica film deposited by AP-PECVD increased with higher deposition rate. We should choose the lower deposition rate experiment parameter to get the denser film. The denser film coated on PC raised the LOI value from 22 to 27. However, the porous film can’t contribute any promotion to LOI value. |
URI: | http://tdr.lib.ntu.edu.tw/jspui/handle/123456789/26439 |
全文授權: | 未授權 |
顯示於系所單位: | 機械工程學系 |
文件中的檔案:
檔案 | 大小 | 格式 | |
---|---|---|---|
ntu-97-1.pdf 目前未授權公開取用 | 6.89 MB | Adobe PDF |
系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。