請用此 Handle URI 來引用此文件:
http://tdr.lib.ntu.edu.tw/jspui/handle/123456789/25174
完整後設資料紀錄
DC 欄位 | 值 | 語言 |
---|---|---|
dc.contributor.advisor | 戴子安(Chi-An Dai) | |
dc.contributor.author | Hung-Wei Lin | en |
dc.contributor.author | 林泓瑋 | zh_TW |
dc.date.accessioned | 2021-06-08T06:04:18Z | - |
dc.date.copyright | 2011-08-18 | |
dc.date.issued | 2011 | |
dc.date.submitted | 2011-08-05 | |
dc.identifier.citation | 1. T. Oho, T. Tonosaki, K. Isomura, K. Ogura, A CO2 sensor operating under high himidity, Journal of Electroanalytical Chemistry, 522 (2002) 173-178.
2. Lin Xia, Zhixiang Wei, Meixiang Wanb, Conducting polymer nanostructures and their application in biosensors, Journal of Colloid and Interface Science, 341 (2010) 1-11. 3. Nicolas Kohut-Svelko,Ste´phanie Reynaud, Re´mi Dedryve`re, Herve´ Martinez, Danielle Gonbeau, and Jeanne Francüois, Study of a nanocomposite based on a conducting polymer: polyaniline, Langmuir, 21 (2005) 1575-1583. 4. Hua Bai and Gaoquan Shi, Gas sensors based on conducting polymers, Sensors, 7 (2007) 267-307. 5. Yang, Z.; Hu, B.; Karasz, F.E, Polymer electroluminescence using ac or reverse dc biasing. Macromolecules, 28 (1995) 6151-6154. 6. Jung, S.H.; Kim, H.K.; Kim, S.H.; Kim, Y.H.; Jeoung, S.C.; Kim, D, Palladium-catalyzed direct synthesis, photophysical properties, and tunable electroluminescence of novel silicon-based alternating copolymers, Macromolecules, 33 (2000) 9277-9288. 7. Gilch, H.G.; Wheelwright, W.L, Polymerization of alpha-halogenated p-xylenes with base, Journal of Polymer Science part A-1-polymer chemistry, 4 (1966) 1337-1349. 8. M.S. Cho, Y.Y. Yun, J.D. Nam, Y. Son, Y. Lee, Effect of magnetic field on electrochemical polymerization of EDOT, Synthetic Metals, 158 (2008) 1043-1046. 9. Jui Hung Chen, Chi-An Dai, Wen-Yen Chiu, Synthesis of highly conductive EDOT copolymer films via oxidative chemical in situ polymerization, Polymer Science, 46 (2008) 1662-1673. 10. Peter A. Levermore, Rui Jin, Xuhua Wang, Lichun Chen, Donal D. C. Bradley and John C. de Mello, High efficiency organic light-emitting diodes with PEDOT-based conducting polymer anodes, Journal of Materials Chemistry, 18 (2008) 4414-4420. 11. Chih-Wei Hu, Kun-Mu Lee, R. Vittal, Dung-Jing Yang, and Kuo-Chuan Ho, A high contrast hybrid electrochromic device containing PEDOT, heptyl viologen, and radical provider TEMPO, Journal of the Electrochemical Society, 157 (2010) 75-78. 12. Irina Schwendeman, Carleton L. Gaupp, Jessica M. Hancock, L. “Bert” Groenendaal, John R. Reynolds, Perfluoroalkanoate-substituted PEDOT for electrochromic device applications, Advanced Functional Materials, 13 (2003) 541-547. 13. V. Martina, K. Ionescu, L. Pigani, F. Terzi, A. Ulrici, C. Zanardi, R. Seeber, Development of an electronic tongue based on a PEDOT-modified voltammetric sensor, Analytical and Bioanalytical Chemistry, 387 (2007) 2101-2110. 14. Tatyana A. Bendikov, Thomas C. Harmon, Long-lived solid state perchlorate ion selective sensor based on doped poly(3,4-ethylenedioxythiophene) (PEDOT) films, Analytica Chimica Acta, 551 (2005) 30-36. 15. Yasuyuki Kiya, Geoffrey R. Hutchison, Jay C. Henderson, Tomoo Sarukawa, Osamu Hatozaki, Noboru Oyama, He´ctor D. Abrun˜a, Elucidation of the redox behavior of 2,5-dimercapto-1,3,4-thiadiazole (DMcT) at poly(3,4-ethylenedioxythiophene) (PEDOT)-modified electrodes and application of the DMcT-PEDOT composite cathodes to lithium/lithium ion batteries, Langmuir, 22 (2006) 10554-10563. 16. Billingham, N.C., Calvert, P.D, Electrically conducting polymers-A polymer science viewpoint, Advances in Polymer Science, 90 (1989) 1-104. 17. B.L. Groenendaal, F. Jonas, D. Freitag, H. Pielartzik. J.R. Reynolds, Poly(3,4-ethylenedioxythiophene) and its derivatives: Past, present, and future, Advanced Materials, 12 (2000) 481-494. 18. Yijie Xia and Jianyong Ouyang, Significant conductivity enhancement of conductive poly(3,4-ethylenedioxythiophene) : poly(styrenesulfonate) films through a treatment with organic carboxylic acids and inorganic acids, Applied materials, 2 (2010) 474-483. 19. Research progress on a novel conductive polymer-poly (3,4-ethylenedioxythiophene) (PEDOT), Journal of Physics: Conference Series 152 (2009). 20. Kiebooms R, Aleshin A, Hutchison K, Wudl F, Thermal and electromagnetic behavior of doped poly(3,4-ethylenedioxythiophene) films, Journal of Physical. Chemistry B, 101 (1997) 11037-11039. 21. Pei Q, Zuccarello G, Ahskog M, Inganas O, Electrochromic and highly stable poly (3,4-ethylenedioxythiophene) switches between opaque blue-black and transparent sky blue, Polymer, 35 (1994) 1347-1351. 22. Yangping Wena, Jingkun Xu, Haohua He, Baoyang Lu, Yuzhen Li, Bin Dong, Electrochemical polymerization of 3,4-ethylenedioxythiophene in aqueous micellar solution containing biocompatible amino acid-based surfactant, Journal of Electroanalytical Chemistry, 634 (2009) 49-58. 23. Yong Lei, Hideki Oohata, Shin-ichi Kuroda, Shintaro Sasaki, Takakazu Yamamoto, Highly electrically conductive poly(3,4-ethylenedioxythiophene) prepared via high-concentration emulsion polymerization, Synthetic Metals, 149 (2005) 211-217. 24. de Leeuw, D.M. Kraakman, P.A. Bongaerts, P.E.G. Mutsaers, C. M. J. Klaassen, Electroplating of conductive polymers for the metallization of insulators, Synthetic Metals, 66 (1994) 263-273. 25. Y.H. Ha et al, Towards a transparent, highly conductive poly(3,4-ethylenedioxythiophene), Advanced functional materials, 14 (2004) 615-622. 26. Nylabder, C.; Armgrath, M.; Lundstrom, I, An ammonia detector based on a conducting polymer, Proceedings of the International Meeting on Chemical Sensors, Fukuoka, Japan, (1983) 203-207. 27. MacDiarmid, A.G, 'Synthetic metals': A novel role for organic polymers (Nobel lecture), Angew. Chem. Int. Edit. 40 (2001) 2581-2590. 28. McGovern, S.T.; Spinks, G.M.; Wallace, G.G, Micro-humidity sensors based on a processablepolyaniline blend, Sensors and Actuators B-chemical, 107 (2005) 657-665. 29. Cho, J.H.; Yu, J.B.; Kim, J.S.; Sohn, S.O.; Lee, D.D.; Huh, J.S, Sensing behaviors of polypyrrole sensor under humidity condition, Sensors and Actuators B-chemical, 108 (2005) 389-392. 30. Ruangchuay, L.; Sirivat, A.; Schwank, J, Selective conductivity response of polypyrrole-based sensor on flammable chemicals, Reactive and Functional. Polymers, 61 (2004) 11-22. 31. Ram, M.K.; Yavuz, O.; Lahsangah, V.; Aldissi, M. CO gas sensing from ultrathin nano-composite conducting polymer film, Sensors and Actuators B-chemical, 106 (2005) 750-757. 32. Nohria, R.; Khillan, R.K.; Su, Y.; Dikshit, R.; Lvov, Y.; Varahramyan, K, Humidity sensor based on ultrathin polyaniline film deposited using layer-by-layer nano-assembly, Sensors and Actuators B-chemical, 114 (2006) 218-222. 33. Agbor, N.E.; Petty, M.C.; Monkman, A.P, Polyaniline thin-films for gas-sensing, Sensors and Actuators B-chemical, 28 (1995) 173-179. 34. Stussi, E.; Cella, S.; Serra, G.; Venier, G.S, Fabrication of conducting polymer patterns for gas sensing by a dry technique, Material Science and Engineering: C, 4 (1996) 27-33. 35. Torsi, L.; Tanese, M.C.; Cioffi, N.; Gallazzi, M.C.; Sabbatini, L.; Zambonin, P.G.; Raos, G.; Meille, S.V.; Giangregorio, M.M, Side-chain role in chemically sensing conducting polymer fieldeffect transistors, Journal of Physical Chemistry B, 107 (2003) 7589-7594. 36. Li, B.; Sauve, G.; Iovu, M.C.; Jeffries-El, M.; Zhang, R.; Cooper, J.; Santhanam, S.; Schultz, L.; Revelli, J.C.; Kusne, A.G.; Kowalewski, T.; Snyder, J.L.; Weiss, L.E.; Fedder, G.K.; McCullough, R.D.; Lambeth, D.N, Volatile organic compound detection using nanostructured copolymers, Nano Letters, 6 (2006) 1598-1602. 37. Liu, H.Q.; Kameoka, J.; Czaplewski, D.A.; Craighead, H.G, Polymeric nanowire chemical sensor, Nano Letters, 4 (2004) 671-675. 38. Lavrik, N.V.; DeRossi, D.; Kazantseva, Z.I.; Nabok, A.V.; Nesterenko, B.A.; Piletsky, S.A.;Kalchenko, V.I.; Shivaniuk, A.N.; Markovskiy, L.N, Composite polyaniline/calixarene Langmuir-Blodgett films for gas sensing, Nanotechnology, 7 (1996) 315-319. 39. Bearzotti, A.; Foglietti, V.; Polzonetti, G.; Iucci, G.; Furlani, A.; Russo, M.V, Investigations on the response to humidity of an interdigitated electrode structure coated with iodine doped polyphenylacetylene, Materials Science and Engineering B, 40 (1996) 1-4. 40. M. Gauthier, A. Chamberland, Solid-state detectors for potentiometric determination of gaseous oxides. 1. Measurement in air, Journal of the Electrochemical Society, 124 (1977) 1579-1583. 41. T. Ishihara, K. Kometani, Y. Mizuhara, Y. Takita, A new type of CO-2 gas sensor based on capacitance changes, Sensors and Actuators B-chemical, 5 (1991) 97-102. 42. S.A. Waghuley, S.M.Yenorkar, S.S Yawale, S.P. Yawale, Application of chemically synthesized conducting polymer-polypyrrole as a carbon dioxide gas sensor, Sensors and Actuators B-chemical, 128 (2008) 366-373. 43. S. Neethirajan, M.S. Freund, D.S. Jayas, C. Shafai, D.J. Thomson, N.D.G. White, Development of carbon dioxide (CO2) sensor for garin quality monitoring, Biosystems Engineering, 106 (2010) 395-404. 44. K. Ogura, H. Shiigi, T. Oho, and T. Tonosaki, A CO2 sensor with polymer composites operating at ordinary temperature, Journal of the Electrochemical Society, 147 (2000) 4351-4355. 45. T. Taka, Synthetic Metals, 5014 (1993) 55-57. 46. Jyongsik Jang, Mincheol Cheng, and Hyeonseok Yoon, Chemical sensors based on highly conductive poly(3,4-ethylenedioxythiophene) nanorods, Advanced Materials, 17 (2005) 1616-1620. 47. Xiaochun Xu, Chunshan Song, Bruce G. Miller, and Alan W. Scaroni, Influence of moisture on CO2 separation from gas mixture by a nanoporous adsorbent based on polyethylenimine-modified molecular sieve MCM-41, Industrial & Engineering Chemistry Research, 44 (2005) 8113-8119. | |
dc.identifier.uri | http://tdr.lib.ntu.edu.tw/jspui/handle/123456789/25174 | - |
dc.description.abstract | 在此研究中,利用快速成膜氧化聚合法合成3,4-乙烯二氧噻吩,並在3,4-乙烯二氧噻吩膜上利用液滴塗布法塗布支鏈型聚乙烯亞胺薄膜,此[3,4-乙烯二氧噻吩]-[支鏈型聚乙烯亞胺]複合膜成膜在黃金指插式電極上,製作成電阻式二氧化碳氣體感測器。在只有3,4-乙烯二氧噻吩薄膜的情形下,感測器對於二氧化碳沒有出現訊號,隨著添加支鏈型聚乙烯亞胺,此感測器對於1000ppm之二氧化碳感測結果,從原來的沒訊號,增加到3.25%,而且訊號大小與添加支鏈型聚乙烯亞胺的量呈現正比關係,此訊號曲線可利用單一指數函數做最適化分析。此感測器在750 ppm到5500 ppm二氧化碳濃度範圍間,其訊號大小與相對應之二氧化碳濃度呈現線性關係;偵測下限經計算約為97 ppm(在訊號/雜訊=3 之標準下);反應時間(t90)以及恢復時間(t90)分別為1264秒以及接近一小時。在溫度以及溼度效應的實驗中,此感測器在室溫以及高濕度的環境下表現出的訊號最大。在重複使用的測試中,此感測器在重複使用三次後其訊號大小並無明顯的衰退趨勢。最後藉由系統改進,使原本較長的恢復時間(接近一小時)縮短至大約10分鐘。 | zh_TW |
dc.description.abstract | In this Study, 3,4-ethylenedioxythiophene (EDOT) was oxidatively polymerized via in-situ polymerization and then fabricated a branched polyethylenimine (BPEI) film on PEDOT by drop casting. The PEDOT-BPEI sensing film which deposited on a gold interdigitated electrode was used as a resistive type carbon dioxide gas sensor. There is no response of the sensor when the sensing film is only a PEDOT monolayer. With adding BPEI, the response to expose to 1000 ppm carbon dioxide increased from nearly none to a value of 3.25% and the response increased with the increasing amount of BPEI. The response curves of PEDOT-BPEI sensing film could be fitted well with single term of exponential expression. The sensor exhibited linear response behavior to carbon dioxide gas at higher concentration (750-5500 ppm). The limit of detection was 97 ppm (signal/noise = 3). The response time (t90) and recovery time (t90) were recorded to be 1264 s and nearly 1 hour, respectively. In the temperature and humidity tests, it could be observed that the optimum operation condition is room temperature and high relative humidity (RH). The reusability test showed that no obvious decay in response for repeatedly (three times) measurements. The long recovery time of nearly 1 hr was shortened to approximately 10 min by heating the sensor during recovery. | en |
dc.description.provenance | Made available in DSpace on 2021-06-08T06:04:18Z (GMT). No. of bitstreams: 1 ntu-100-R98524081-1.pdf: 1256784 bytes, checksum: 86f7c20adaf5bf38cc274b5b8730a3da (MD5) Previous issue date: 2011 | en |
dc.description.tableofcontents | 誌謝 I
摘要 II Abstract III Contents IV List of Tables VI List of Figures VII Chapter 1 Introduction 1 Chapter 2 Literature Review 3 2.1 Conducting polymer 3 2.1.1 Introduction 3 2.1.2 Synthesis of conducting polymers 3 2.2 PEDOT 5 2.2.1 Introduction 5 2.2.2 Excellent characteristics of PEDOT [19] 6 2.2.3 Synthesis of PEDOT 6 2.3 Conducting polymers in gas sensor applications 9 2.3.1 Introduction 9 2.3.2 Preparation of conducting polymer sensing films 10 2.3.3 Sensing materials 12 2.3.4 Chemiresistors 13 2.3.5 The advantages and disadvantages of using conducting polymers as gas sensors 14 2.4 Conducting polymers as carbon dioxide gas sensors 17 2.4.1 Introduction 17 2.4.2 Carbon dioxide sensor based on polypyrrole [42] 17 2.4.3 Carbon dioxide sensor based on polyaniline boronic acid [43] 19 2.4.4 Carbon dioxide sensor based on emeraldine base-polyaniline / poly(vinyl alcohol) [44] 21 Chapter 3 Experiment 24 3.1 Experiment materials 24 3.2 Experiment instruments 26 3.3 Experiment procedure 27 3.4 Experiment methods 28 3.4.1 Preparation of the PEDOT-BPEI composite film 28 3.4.2 Preparation of the PEDOT-TCA-BPEI composite film 29 3.4.3 FT-IR 29 3.4.4 AFM 30 3.4.5 UV-vis 30 3.4.6 Gas sensing 30 Chapter 4 Result and Discussion 33 4.1 Material character properties 33 4.1.1 FT-IR 33 4.1.2 AFM 33 4.1.3 UV-vis 34 4.2 Response of the PEDOT-BPEI sensing film to CO2 gas 35 4.3 Response of the PEDOT-TCA-BPEI sensing film to CO2 gas 35 4.4 Proposed mechanism 36 4.5 Transit responses of PEDOT-BPEI sensing film 38 4.6 Gas sensing characteristics 39 4.7 Temperature effect and humidity effect 40 4.8 Selectivity and reusability test 42 4.9 System improvement experiment 43 Chapter 5 Conclusions 44 Chapter 6 References 46 | |
dc.language.iso | en | |
dc.title | 以原位聚合法合成導電高分子複合膜
應用於二氧化碳氣體感測器之研究 | zh_TW |
dc.title | In-Situ Synthesis of Conducting Polymer
Composite Film as a CO2 Gas Sensor | en |
dc.type | Thesis | |
dc.date.schoolyear | 99-2 | |
dc.description.degree | 碩士 | |
dc.contributor.oralexamcommittee | 何國川(Kuo-Chuan Ho),張培仁(Pei-Zen Chang),施文彬(Wen-Pin Shih) | |
dc.subject.keyword | 導電高分子,3,4-乙烯二氧噻,吩,二氧化碳氣體感測器, | zh_TW |
dc.subject.keyword | conducting polymer,PEDOT,CO2 gas sensor, | en |
dc.relation.page | 80 | |
dc.rights.note | 未授權 | |
dc.date.accepted | 2011-08-05 | |
dc.contributor.author-college | 工學院 | zh_TW |
dc.contributor.author-dept | 化學工程學研究所 | zh_TW |
顯示於系所單位: | 化學工程學系 |
文件中的檔案:
檔案 | 大小 | 格式 | |
---|---|---|---|
ntu-100-1.pdf 目前未授權公開取用 | 1.23 MB | Adobe PDF |
系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。