請用此 Handle URI 來引用此文件:
http://tdr.lib.ntu.edu.tw/jspui/handle/123456789/18484
完整後設資料紀錄
DC 欄位 | 值 | 語言 |
---|---|---|
dc.contributor.advisor | 姜昱至 | |
dc.contributor.author | Szu-Ying Huang | en |
dc.contributor.author | 黃思穎 | zh_TW |
dc.date.accessioned | 2021-06-08T01:07:35Z | - |
dc.date.copyright | 2014-10-15 | |
dc.date.issued | 2014 | |
dc.date.submitted | 2014-08-19 | |
dc.identifier.citation | 1.紀乃智,王宏欽,戴怡佳,林妤珊,王乃亭,劉秀月., 陳.蕭.嚴.楊.詹.邱.蔡.陳.吳., 台灣地區兒童及青少年口腔狀況調查. 國民健康局九十四與九十五年度科技研究發展計畫, 2007.
2.Featherstone, J.D., The science and practice of caries prevention. J Am Dent Assoc. , 2000. 131: p. 887-99. 3.Guo, M.K., et al., Effect of water fluoridation on prevalence of dental caries in Chung-Hsing New Village, Taiwan, after 9 years. Taiwan Yi Xue Hui Za Zhi., 1984. 83: p. 1035-43. 4.Jenkins, G.N., Review of fluoride research since 1959. Arch Oral Biol. , 1999. 44: p. 985-92. 5.Rolla, G., On the role of calcium fluoride in the cariostatic mechanism of fluoride. Acta Odontol Scand., 1988. 46(341-5). 6.Fejerskov, O., F. Manji, and V. Baelum, The nature and mechanisms of dental fluorosis in man. J Dent Res. , 1990. 69: p. 692-700. 7.Cooray, U., A Note On Mode of action of fluoride and the caries process. 2011. 8.R. W. Phillips , 高., 翁秀和, 牙科材料學”, 第五版. 1990. 9.IR, R., A review of direct orthodontic bonding. Br Dent J, 1975. 2: p. 171. 10.Rosin-Grget, K., et al., The cariostatic mechanisms of fluoride. Acta Med Acad, 2013. 42(2): p. 179-88. 11.Mohammed, N.R., et al., Effects of fluoride on in vitro enamel demineralization analyzed by (1)(9)F MAS-NMR. Caries Res, 2013. 47(5): p. 421-8. 12.郭敏光, 含氟無填料 Bis-GMA 樹脂之氟離子釋出能力. Chinese Dental Juornal(中 華 牙 誌 ) 1997. 16(4): p. 227-241. 13.Crivello, J., Applications of phototinitiated cationic polymerization in coatings. Journal of Coatings Technology, 1991. 63(793): p. 35–38. 14.Dittenber, D.B. and H.V.S. GangaRao, Critical review of recent publications on use of natural composites in infrastructure. Composites Part A: Applied Science and Manufacturing, 2012. 43(8): p. 1419-1429. 15.Mo, S.S., et al., The microfloral analysis of secondary caries biofilm around Class I and Class II composite and amalgam fillings. BMC Infect Dis, 2010. 10: p. 241. 16.P.N.R. Pereira, S. Inokoshi, and J. Tagami, In vitro secondary caries inhibition around fluoride releasing materials. Journal of Dentistry, 1990. 26(5-6): p. 505-510. 17.Peris, A.R., et al., Adhesive systems and secondary caries formation: Assessment of dentin bond strength, caries lesions depth and fluoride release. Dent Mater, 2007. 23(3): p. 308-16. 18.Chen, C.-Y., et al., Low-shrinkage visible-light-curable urethane-modified epoxy acrylate/SiO2 composites as dental restorative materials. Composites Science and Technology, 2008. 68(13): p. 2811-2817. 19.Beyth, N., A.J. Domb, and E.I. Weiss, An in vitro quantitative antibacterial analysis of amalgam and composite resins. J Dent, 2007. 35(3): p. 201-6. 20.Arends J, D.G., Dijkman AG. , Review of fluoride release and secondary caries reduction by fluoridating composites. . Adv Dent Res, 1995. 9: p. 367-76. 21.張進順, 防齲策略及氟化物應用. 台灣牙醫界, 2007. 26(10): p. 28-31. 22.Silverstone LM. Dental caries. New York: MacMillian, I., Dental caries. New York: MacMillian, 1981. 23.Wiegand, A., W. Buchalla, and T. Attin, Review on fluoride-releasing restorative materials--fluoride release and uptake characteristics, antibacterial activity and influence on caries formation. Dent Mater, 2007. 23(3): p. 343-62. 24.Fejerskov O, C.B.I.F.O., Ekstrand J, Burt BA, editors., Dynamics of caries lesion formation. Fluoride in dentistry. , 1996: p. 187–213. 25.Edgar WM, H.S., Role of saliva in caries models. Adv Dent Res, 1995. 9: p. 235-2238. 26.Dijkman A, H.E., Ruben J, Arends J. , Remineralization of human enamel in situ after 3 months: the effect of not brushing versus the effect of an F dentifrice and an F-free dentifrice. . Caries Res, 1990. 24: p. 263-266. 27.L. SAVARINO, M.C., S. STEA, D. CAVEDAGNA, M. E. DONATI, A. PIZZOFERRATO and M. VISENTIN In vitro investigation of aluminum and fluoride release from compomers, conventional and resin-modified glass-ionomer cements: A standardized approach. J. Biomater. Sci. Polymer Edn, 2000. 11(3): p. 289-300. 28.Acta, R.G., On the role of calicium fluoride in the cariostatic mechanism of fluoride. Odont Scand, 1988. 46: p. 341-345. 29.Toumba KJ, C.M., Slow-release fluoride. Caries Res 1993. 27: p. 43-46. 30.J., T.C., Review on fluoride, with special emphasis on calcium fluoride mechanisms in caries prevention. . European Journal of Oral Sciences, 1997. 105(5): p. 461-465. 31.Qvist V, L.L., Poulsen A, Teglers PT., Longevity and cariostatic effects of everyday conventional glass-ionomer and amalgam restorations in primary teeth:three-year results. J Dent Res 1997. 76: p. 1387-1396. 32.W. Gaoa, R.J.S., Fluoride releaseuptake of conventional and resin-modifed glass ionomers, and compomers. Journal of Dentistry 2001. 29: p. 301-306. 33.Xu, X. and J.O. Burgess, Compressive strength, fluoride release and recharge of fluoride-releasing materials. Biomaterials, 2003. 24(14): p. 2451-2461. 34.Verbeeck RM, D.M.E., Marks LA, De Moor RJ, De Witte AM, Trimpeneers LM. , Fluoride release process of (resin-modified) glass-ionomer cements versus (polyacid-modified) composite resins. Biomaterials, 1998. 19: p. 509-19. 35.Lee SY, D.D., Huang HM, Shih YH. , Fluoride ion diffusion from a glass-ionomer cement. J Oral Rehabil 2000. 27: p. 576-86. 36.Williams JA, B.R., Pearson GJ. , A long term study of fluoride release from metal-containing conventional and resin-modified glass-ionomer cements. J Oral Rehabil, 2001. 28: p. 41-7. 37.Creanor SL, C.L., Saunders WP, Strang R, Foye RH. , Fluoride uptake and release characteristics of glass ionomer cements. Caries Res, 1994. 28: p. 322-8. 38.Weerasooriya, R., Surface complexation modeling of fluoride adsorption onto kaolinite, Colloids and Surface A. 1998. 144: p. 266-273. 39.Weerasooriya, R., Modeling Anion Adsorption on Kaolinite, Colloids and Surface A. Journal of Colloid and Interface Science, 1999. 213: p. 395-399. 40.廖建勛, 納米高分子複合材料. 工業材料, 1997. 108(125). 41.Jung, I.H., et al., Effect of (-)-epigallocatechin-3-gallate on maintaining the periodontal ligament cell viability of avulsed teeth: a preliminary study. J Periodontal Implant Sci, 2011. 41(1): p. 10-6. 42.Nakagawa, K., et al., Tea catechin supplementation increases antioxidant capacity and prevents phospholipid hydroperoxidation in plasma of humans. J Agric Food Chem. 1999;47:3967-73., 1999. 47: p. 3967-73. 43.Xu, X., X.D. Zhou, and C.D. Wu, The tea catechin epigallocatechin gallate suppresses cariogenic virulence factors of Streptococcus mutans. Antimicrob Agents Chemother, 2011. 55(3): p. 1229-36. 44.Sato, T. and G. Miyata, The nutraceutical benefit, part iv: garlic. Nutrition, 2000. 16(9): p. 787-8. 45.Yang, C.S., P. Maliakal, and X. Meng, Inhibition of carcinogenesis by tea. Annu Rev Pharmacol Toxicol, 2002. 42: p. 25-54. 46.Gordon, N.C. and D.W. Wareham, Antimicrobial activity of the green tea polyphenol (-)-epigallocatechin-3-gallate (EGCG) against clinical isolates of Stenotrophomonas maltophilia. Int J Antimicrob Agents, 2010. 36(2): p. 129-31. 47.Gradisar, H., et al., Green tea catechins inhibit bacterial DNA gyrase by interaction with its ATP binding site. J Med Chem., 2007. 50: p. 264-71. 48.Hirasawa, M., K. Takada, and S. Otake, Inhibition of acid production in dental plaque bacteria by green tea catechins. Caries Res, 2006. 40(3): p. 265-70. 49.Kato, M.T., et al., Gels containing MMP inhibitors prevent dental erosion in situ. J Dent Res, 2010. 89(5): p. 468-72. 50.Chung, k.-c., Polymer-Smectic Clay Nanocomposite as Dental Restoratives. 2003. 51.Tsai, Y.-R., Development of Bacteriostatic Epigallocatechin Gallate Modified Dental Composite Resin. 2013. 52.Chan, W.D., et al., Fluoride release from dental cements and composites: a mechanistic study. Dent Mater, 2006. 22(4): p. 366-73. 53.Mutlu ozcan, S.H.B., Renata Marques Melo,Graziela Avila Prado Galhano,Marco Antonio Bottino, Effect of surface conditioning methods on the microtensile bond strength of resin composite to composite after aging conditions. Dental Materials, 2007. 23: p. 1276-1282. 54.Liu, B.Y., E.C.M. Lo, and C.M.T. Li, Effect of silver and fluoride ions on enamel demineralization: a quantitative study using micro-computed tomography. Australian Dental Journal, 2012. 57(1): p. 65-70. 55.Lo, E.C., Q.H. Zhi, and A. Itthagarun, Comparing two quantitative methods for studying remineralization of artificial caries. J Dent, 2010. 38(4): p. 352-9. 56.Zhi, Q.H., E.C. Lo, and A.C. Kwok, An in vitro study of silver and fluoride ions on remineralization of demineralized enamel and dentine. Aust Dent J, 2013. 58(1): p. 50-6. 57.Diamanti, I., et al., Effect of fluoride and of calcium sodium phosphosilicate toothpastes on pre-softened dentin demineralization and remineralization in vitro. J Dent, 2010. 38(8): p. 671-7. 58.Liu, B.Y., E.C. Lo, and C.M. Li, Effect of silver and fluoride ions on enamel demineralization: a quantitative study using micro-computed tomography. Aust Dent J, 2012. 57(1): p. 65-70. 59.Torlakovic, L., et al., Clinical color intensity of white spot lesions might be a better predictor of enamel demineralization depth than traditional clinical grading. American Journal of Orthodontics and Dentofacial Orthopedics, 2012. 142(2): p. 191-198. 60.Hamilton IR, B.G., Fluoride effects on oral bacteria. Fluoride in dentistry. Copenhagen: Munksgaard, 1996: p. 230–51. 61.EM., G., Developing pathways for oral care in elders: evidence-based interventions for dental caries prevention in dentate elders. . Gerodontology. , 2014. 31(1): p. 31-6. 62.Itota T, N.S., Iwai Y, Konishi N, Nagamine M, Torii Y., Inhibition of artificial secondary caries by fluoride-releasing adhesives on root dentin. . Journal of oral rehabilitation. , 2002. 29: p. 523-7. 63.Yamamoto, H., et al., Fluorine uptake into the human tooth from a thin layer of F-releasing material. Nuclear Instruments and Methods in Physics Research Section B: Beam Interactions with Materials and Atoms, 2007. 260(1): p. 194-200. 64.Yli-Urpo H, V.P., Narhi TO, Forsback AP, Vakiparta M., Release of silica, calcium, phosphorus, and fluoride from glass ionomer cement containing bioactive glass. J Biomater Appl, 2004. 19: p. 5-20. 65.Xu HH, E.F., Antonucci JM, Schumacher GE, Ives LK., Dental resin composites containing ceramic whiskers and precured glass ionomer particles. Dent Mater 2000. 16: p. 356-63. 66.Xu HH, E.F., Antonucci JM, Flaim GM. , Single-crystalline ceramic whisker-reinforced carboxylic acid–resin composites with fluoride release. Oper Dent 2000. 25: p. 90-7. 67.Asmussen E, P.A., Long-term fluoride release from a glass ionomer cement, a compomer, and from experimental resin composites. Acta Odontol Scand., 2002. 60: p. 93-7. 68.Dhondt CL, D.M.E., Verbeeck RM. , Fluoride release from glass ionomer activated with fluoride solutions. . J Dent Res, 2001;. 80: p. 1402-6. 69.江顯雄, 郭., <16-241.pdf>. Chinese Dental Juornal(中 華 牙 誌 ), 1997. 16(4): p. 227-241. 70.Al-Naimi, O.T., et al., Fluoride release for restorative materials and its effect on biofilm formation in natural saliva. J Mater Sci Mater Med, 2008. 19(3): p. 1243-8. 71.El- Mehadawi SM, D.F., Zullo T. , Fluoride ion release from ultraviolet light-cured sealant containg sodium fluoride. Pediatr Dent, 1985. 7: p. 287-291. 72.Han L, C.E., Li M, Niwano K, Ab N, Okamoto A, et al., Effect of fluoride mouth rinse on fluoride releasing and recharging from aesthetic dental materials. Dent Mater J, 2002. 21: p. 285-95. 73.Hickel R, D.W., Janda R, et al. , New direct restorative mat erials. FDI Commission Project Int Dent J, 1998. 48: p. 315. 74.Melo MA, M.W., Passos VF, Lima JP, Rodrigues LK. F . luoride releasing and enamel demineralization around orthodontic brackets by fluoride-releasing composite containing nanoparticles. . Clinical oral investigations., 2013. 75.Ekstrand J, F.O., Silverstone LM, editors. , Fluoride in Dentistry. Copenhagen: Munksgaard, 1988: p. 96. 76.Dijkman GEHM, A.J., Long term fluoride release of visible light-activated composites in vitro: a correlation with in situ demineralization data. Caries Res 1997. 27: p. 117-23. 77.Wang, Y.-L., et al., Characterization, fluoride release and recharge properties of polymer–kaolinite nanocomposite resins. Composites Science and Technology, 2007. 67(15-16): p. 3409-3416. 78.Tammaro L, V.V., Calarco A, Petillo O, Riccitiello F, Peluso G. , Effect of layered double hydroxide intercalated with fluoride ions on the physical, biological and release properties of a dental composite resin. . Journal of dentistry., 2014. 42: p. 60-7. 79.Ganss, C., J. Klimek, and C. Starck, Quantitative analysis of the impact of the organic matrix on the fluoride effect on erosion progression in human dentine using longitudinal microradiography. Arch Oral Biol, 2004. 49(11): p. 931-5. 80.黄彬, 陈., <绿茶提取物表没食子儿茶素没食子酸酯对酸蚀症牙本质胶原降解作用的初步研究.pdf>. 华西口腔医学杂志, 2012. 30(5): p. 549-551. 81.Manhart, J., Mechanical Properties of New Composite Restorative Materials,. J Biomed Mater Res (Appl Biomater), 2000. 53: p. 353-361. 82.LeBaron, P.C., Polymer-layered silicate nanocomposites: an overview. Applied Clay Science,, 1999. 15: p. 11-29. 83.M. Atai, D.C.W., Z. Atai. , Shrinkage strain-rates of dental resin-monomer and composite systems. . Biomaterials, 2005. 26: p. 5010-5020. 84.Odian., G., Principles of polymerization. John Wiley & Sons, Inc. 4th ed. 2004: p. 285. 85.Maolinbay M, E.-M.Y., Antonuk L, Jee K, Nassif S, Rong X and Zhao Q, Additive noise properties of active matrix flat-panel imagers Med. Phys. , 2000. 27: p. 1841-54. 86.Davis, G.R., A.N. Evershed, and D. Mills, Quantitative high contrast X-ray microtomography for dental research. J Dent, 2013. 41(5): p. 475-82. 87.Sullivan RJ, C.A., Blake-Haskins, Zhang YP,Gaffar A. , In vivo detection of calcium from dicalcium phosphate dehydrate dentifrices in demineralized human enamel and plaque. Adv Dent Res 1997;. 11: p. 380-7. 88.Tseng, P.-W., Inference of the remineralized microstructure of enamel etched with various phosphoric acid concentrations. Master Program of Graduate Institute of Dentistry College of Oral Medicine Taipei Medical University, 2007. 89.T., I., Prevention of progression of dental erosion by professional and individual prophylactic measures. . Eur J Oral Sci 1996. 104: p. 215-30. 90.Sato Y, S.T., Niwa M, Aoki H. , Precipitation of octacalcium phosphates on artificial enamel in artificial saliva. . J Mater Sci Mater Med, 2006. 17: p. 1173-7. | |
dc.identifier.uri | http://tdr.lib.ntu.edu.tw/jspui/handle/123456789/18484 | - |
dc.description.abstract | 牙科複合樹脂(Composite resin)因在美觀上的優勢,故已漸漸取代汞齊合
金(amlagam)成為臨床填補的主要材料,但材料本身缺乏抗齲蝕能力,無法持 續釋放氟素(Fluoride),氟素有助於鞏固牙齒及防止齲齒的功效,並能減少牙 齒因酸蝕而產生的去礦化作用與促進牙齒再礦化作用。加上在光照聚合之後複合 樹脂會產生體積的收縮(Shinkage),使牙齒與填補物之間產生縫隙(gap),造成微滲漏(microleackage),細菌便在此滋長導致材料鬆動,最後在邊緣處造成繼發性齲齒(secondary caries),而使其在應用上受到限制 。 因此本研究目的為研發氟化兒茶素改質之牙科複合樹脂,利用高嶺石(Kaolinite)的層狀結構,其層間對氟離子良好的吸附效果,使材料能釋放並再吸收更多氟素。此外為減少聚合收縮量,基質為改質之環氧丙烯酸樹脂(epoxyacrylate),因分子量較大且此多官能基壓克力單體照光聚合後會形成交聯網狀結構,可使收縮量明顯降低。另一方面加入兒茶素(EGCG)希望能提升材料抵抗去礦化與促進再礦化效果。 本研究分為三部分進行,第一部分為合成氟化兒茶素改質之牙科複合樹脂。包含樹脂有機基質合成、表沒食子兒茶素沒食子酸酯(EGCG)改質、氟化高嶺土無機填料合成與氧化鋁無機填料合成。 第二部分為材料分析與測試:測量氟離子釋放濃度與再釋放濃度、並比較其 機械性質與老化對材料的影響。 第三部分為建立一套標準化檢視人工齲齒模型(Artificial secondary caries model)實驗模式,以去礦化與再礦化(Demineralization and remineralization)循環模擬口內填補材料後之環境,利用微米級電腦斷層掃描、掃瞄式電子顯微儀觀察樣本表面變化,並搭配電腦軟體定量分析計算出去礦化體積(Demineralization volume)與平均病灶深度(Average lesion depth)。藉此評估並比較材料抵抗齲齒的能力。 實驗結果顯示本實驗研發之氟化兒茶素改質之牙科複合樹脂具有比市售材料更高的釋氟量、更低的聚合收縮、更好的抵抗齲蝕能力,故在臨床應用上對於預防繼發性齲齒發展具有相當的潛力。而其物理性質及機械性質略低於市售產品,因此仍須針對使用時機與角色有所調整。 | zh_TW |
dc.description.abstract | The use of dental composite resin material is increasing rapidly in recent years.
This increase is attributed primarily to demand for improved esthetics. Present filling materials are hard to avoid the re-invasion of caries, and the ability of fluoride release was limited. The role of fluoride in the prevention of caries is well known in dentistry, which is generally thought to help teeth remineralization, inhibit teeth demineralization, antibacterial effects and even anti erosion effects. Otherwise, because of its polymerization shrinkage to cause marginal leakage, and easily for bacteria adhesion, it still didn’t have the resistant ability to secondary caries. And it limited the success of composite restoration. The object of this study was to development a novel Fluorinated Epigallocatechin Gallate Modified Dental Composite Resin. Kaolinite (Al2Si2O5(OH)4), a clay mineral, has been known for its ability to carry and absorption of fluoride due to its layered aluminosilicate structure. And urethane-modified epoxy acrylates was used as resin matrix to form low-shrinking composites, because of their relatively high molecular weight and cohesive energy density resulting from the presence of the urethane group. We also add epigallocatechin gallate(EGCG) to increase the ability of remineralization. This study was carried out in three parts: Part 1: Development of Fluorinated Epigallocatechin Gallate Modified Dental Composite Resin. Including matrix formation, EGCG modification , and synthesis of fluorinited fillers and aluminum oxide fillers. Part 2 : To assess the fluoride release and recharge, and the physical properties, including the aging effect. Part 3: An artificial caries model was established for the demineralization and remineralization test. We qualitatively and quantitatively examine the demineralization and remineralization of the restorative teeth sample by the high-resolution micro computed tomography (Micro-CT) and scanning electron microscope (SEM). We calculate the demineralization volume and average lesion depth with the software to compare the anti-demineralization ability of these materials. With the results, we can conclude that the Fluorinated Epigallocatechin Gallate Modified Dental Composite Resin has more fluoride release and recharge, lower polymerization shrinkage, and great potential for caries prevention. Because the mechanical properties is not ideal , more studies should be explored. | en |
dc.description.provenance | Made available in DSpace on 2021-06-08T01:07:35Z (GMT). No. of bitstreams: 1 ntu-103-R00422002-1.pdf: 41026105 bytes, checksum: 887de947dc2b5d79b41d35f05c7d3e15 (MD5) Previous issue date: 2014 | en |
dc.description.tableofcontents | 中文摘要 ••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••i
Abstract •••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••iii 目錄•••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••v 圖附錄••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••ix 表附錄••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••xiii 第一章 緒論••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••1 1-1 齲齒••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••1 1-1-1 前言••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••1 1-1-2 致病機制••••••••••••••••••••••••••••••••••••••••••••••••••••••1 1-2 牙科用複合樹脂••••••••••••••••••••••••••••••••••••••••••••••••••3 1-2-1 發展••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••3 1-2-2 牙科複合樹脂基本組成••••••••••••••••••••••••••••••••••4 1-2-3 理想的牙科綴補材料••••••••••••••••••••••••••••••••••••••7 1-2-4 複合樹脂填補物與繼發性齲齒的關係•••••••••••••••8 1-3 抗齲齒成分之原理與應用•••••••••••••••••••••••••••••••••••••10 1-3-1 氟化物•••••••••••••••••••••••••••••••••••••••••••••••••••••••••10 1-3-1-1 氟化物防齲的認識•••••••••••••••••••••••••••••••••••10 1-3-1-2 氟化物抑制齲齒的機制•••••••••••••••••••••••••••••11 1-3-1-3 釋放氟素的填補材料••••••••••••••••••••••••••••••••13 1-3-1-4 高嶺石的構造••••••••••••••••••••••••••••••••••••••••••16 1-3-1-5 高嶺石吸附氟化物(Fluoride)理論模型•••17 1-3-2兒茶素之(Catechin)表沒食子兒茶酚沒食子酸(epigallocatechin gallate,EGCG)••••••••••••••••••••••••••••••••••••••••••••••••••••••••19 第二章 實驗動機與目的••••••••••••••••••••••••••••••••••••••••••••••••••22 第三章 實驗材料與方法••••••••••••••••••••••••••••••••••••••••••••••••••23 3-1 氟化兒茶素改質之複合樹脂系統合成•••••••••••••••••••••••24 3-1-1 樹脂有機基質合成•••••••••••••••••••••••••••••••••••••••••••24 3-1-1-1 表沒食子兒茶素沒食子酸酯(EGCG)改質••••••25 3-1-2 氟化高嶺土無機填料合成••••••••••••••••••••••••••••••••••26 3-1-2-1 高嶺土/N-甲基甲醯胺複合物(K-NMF)之製 備••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••26 3-1-2-2 高嶺土/丙烯醯胺含氟複合物之製備•••••••••••••27 3-1-2-3 高嶺土/丙烯醯胺含氟複合物之矽烷化處理•••27 3-1-3 氧化鋁無機填料合成•••••••••••••••••••••••••••••••••••••••••28 3-1-4 氟化兒茶素改質之複合樹脂合成•••••••••••••••••••••••••28 3-2 材料分析與測試••••••••••••••••••••••••••••••••••••••••••••••••••••••29 3-2-1 樹脂錠片樣本之製作••••••••••••••••••••••••••••••••••••••••••29 3-2-2 氟離子釋放測試•••••••••••••••••••••••••••••••••••••••••••••••••30 3-2-2-1 氟離子釋放濃度測量•••••••••••••••••••••••••••••••••••••30 3-2-2-2 氟離子再吸收後的釋放測試••••••••••••••••••••••••••••30 3-2-3 複合樹脂之物理性質測試••••••••••••••••••••••••••••••••••••••30 3-2-3-1 直徑抗拉強度分析(DTs)••••••••••••••••••••••••••••••••31 3-2-3-2 微硬度(Micro-hardness)測試•••••••••••••••••31 3-2-3-3 抗彎強度(flexural strength)•••••••••••••••••32 3-2-3-4 聚合收縮分析測試••••••••••••••••••••••••••••••••••••••••••33 3-2-3-5老化試驗•••••••••••••••••••••••••••••••••••••••••••••••••••••••••33 3-3 人工齲齒模型••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••34 3-3-1 牙齒收集與樣本備製•••••••••••••••••••••••••••••••••••••••••••••34 3-3-2 再礦化與去礦化溶液備製•••••••••••••••••••••••••••••••••••••••34 3-3-3 微米級電腦斷層掃描造影與分析••••••••••••••••••••••••••••••35 3-3-4 掃瞄式電子顯微觀察(SEM)與能量色散型X 射線螢光 分析(EDS)•••••••••••••••••••••••••••••••••••••••••••••••••••••••••••36 3-3-5 人造齲齒模型之微硬度測試(Microhardness)••••36 第四章 實驗結果•••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••37 4-1 氟化兒茶素改質之牙科複合樹脂•••••••••••••••••••••••••••••••••••••37 4-1-1 樹脂有機基質合成與表沒食子兒茶素沒食子酸酯(EGC G)改質••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••37 4-1-2 氟化高嶺土無機填料合成•••••••••••••••••••••••••••••••••••••••••38 4-1-3 氧化鋁無機填料合成••••••••••••••••••••••••••••••••••••••••••••••••38 4-1-4 氟化兒茶素改質之牙科複合樹脂合成與材料分組•••••••••39 4-2 材料分析與測試•••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••39 4-2-1 樹脂錠片樣本之製作•••••••••••••••••••••••••••••••••••••••••••••••••39 4-2-2 氟離子釋放與再吸收•••••••••••••••••••••••••••••••••••••••••••••••••39 4-2-3 複合樹脂之物理性質測試•••••••••••••••••••••••••••••••••••••••••••41 4-2-3-1 直徑抗拉強度分析(DTs)•••••••••••••••••••••••••••••••••••••41 4-2-3-2 微硬度(Micro-hardness)測試••••••••••••••••••••••42 4-2-3-3 抗彎強度(flexural strength)與撓曲模數(Flexual modulus)••••••••••••••••••••••••••••••••••••••••••••••••••••••••42 4-2-3-4 聚合收縮(polymerization shrinkage)分析測 試••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••43 4-3 人工齲齒模型••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••44 4-3-1 牙齒收集與樣本備製••••••••••••••••••••••••••••••••••••••••••••••••••44 4-3-2 微米級電腦斷層掃描造影與分析••••••••••••••••••••••••••••••••••44 4-3-3 掃瞄式電子顯微觀察(SEM)與能量色散型X射線螢光分析 (EDS)••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••45 4-3-4 人造齲齒模型之微硬度測試(Microhardness)•••••••••45 第五章 討論••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••46 5-1 氟離子釋放與再吸收•••••••••••••••••••••••••••••••••••••••••••••••••••••••••46 5-2 表沒食子兒茶素沒食子酸酯(EGCG)的影響••••••••••••••••••••••••••50 5-3 複合樹脂之物理性質測試•••••••••••••••••••••••••••••••••••••••••••••••••••52 5-3-1 直徑抗拉強度分析(DTs)•••••••••••••••••••••••••••••••••••••••••••••52 5-3-2 微硬度(Micro-hardness)•••••••••••••••••••••••••••••••••••••52 5-3-3 抗彎強度(flexural strength)••••••••••••••••••••••••••••••53 5-3-4 聚合收縮(polymerization shrinkage)分析••••••••••54 5-4 人工齲齒模型••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••55 5-4-1 微米級電腦斷層掃描造影與分析(Micro CT)••••••••••••••••55 5-4-2 掃瞄式電子顯微觀察(SEM)/能量色散型X 射線螢光分析( EDS)••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••56 第六章 結論••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••59 參考文獻•••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••••61 | |
dc.language.iso | zh-TW | |
dc.title | 研發氟化兒茶素改質之牙科複合樹脂 | zh_TW |
dc.title | Development of Fluorinated Epigallocatechin Gallate Modified Dental Composite Resin | en |
dc.type | Thesis | |
dc.date.schoolyear | 102-2 | |
dc.description.degree | 碩士 | |
dc.contributor.oralexamcommittee | 陳敏慧,高嘉澤,陳賢燁 | |
dc.subject.keyword | 複合樹脂,繼發性齲齒,兒茶素,氟素,高嶺土,人工齲齒模型,去礦化與再礦化, | zh_TW |
dc.subject.keyword | Composite resin,secondary caries,epigallocatechin gallate,fluoride,kaolinite,artificial caries model,demineralization and remineralization, | en |
dc.relation.page | 111 | |
dc.rights.note | 未授權 | |
dc.date.accepted | 2014-08-19 | |
dc.contributor.author-college | 牙醫專業學院 | zh_TW |
dc.contributor.author-dept | 臨床牙醫學研究所 | zh_TW |
顯示於系所單位: | 臨床牙醫學研究所 |
文件中的檔案:
檔案 | 大小 | 格式 | |
---|---|---|---|
ntu-103-1.pdf 目前未授權公開取用 | 40.06 MB | Adobe PDF |
系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。