dc.contributor.advisor | 陳洵毅 | |
dc.contributor.author | Ho-Wei Chan | en |
dc.contributor.author | 詹賀惟 | zh_TW |
dc.date.accessioned | 2021-06-17T08:08:49Z | - |
dc.date.available | 2019-08-20 | |
dc.date.copyright | 2019-08-20 | |
dc.date.issued | 2019 | |
dc.date.submitted | 2019-08-16 | |
dc.identifier.citation | Anselmi-Tamburini, U., J. E. Garay, Z. A. Munir, A. Tacca, F. Maglia, and G. Spinolo, 2004: Spark plasma sintering and characterization of bulk nanostructured fully stabilized zirconia: Part I. Densification studies. Journal of Materials Research, 19, 3255-3262.
Anusavice, K. J., C. Shen, and H. R. Rawls, 2012: Phillips' science of dental materials. Elsevier Health Sciences. ASTM. Standard Specification for High PurityDense Yttria Tetragonal Zirconium Oxide polycrystal(Y-TZP) for surgical Application. Annual Book forASTM Standard, F1873-98 ASTM Boukamp, B. A., and H. J. Bouwmeester, 2003: Interpretation of the Gerischer impedance in solid state ionics. Solid state ionics, 157, 29-33. Caliman, L. B., E. Bichaud, P. Soudant, D. Gouvea, and M. C. Steil, 2015: A simple flash sintering setup under applied mechanical stress and controlled atmosphere. MethodsX, 2, 392-398. Chen, F., and Coauthors, 2015: Field assisted sintering of graphene reinforced zirconia ceramics. Ceramics International, 41, 6113-6116. Chen, I. W., and X. H. Wang, 2000: Sintering dense nanocrystalline ceramics without final-stage grain growth. Nature, 404, 168-171. Chen, W., U. Anselmi-Tamburini, J. E. Garay, J. R. Groza, and Z. A. Munir, 2005: Fundamental investigations on the spark plasma sintering/synthesis process - I. Effect of dc pulsing on reactivity. Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing, 394, 132-138. Chu, M. Y., L. C. Dejonghe, M. K. F. Lin, and F. J. T. Lin, 1991: PRECOARSENING TO IMPROVE MICROSTRUCTURE AND SINTERING OF POWDER COMPACTS. Journal of the American Ceramic Society, 74, 2902-2911. Cologna, M., and R. Raj, 2011: Surface Diffusion-Controlled Neck Growth Kinetics in Early Stage Sintering of Zirconia, with and without Applied DC Electrical Field. Journal of the American Ceramic Society, 94, 391-395. Cologna, M., B. Rashkova, and R. Raj, 2010: Flash Sintering of Nanograin Zirconia in <5 s at 850°C. Journal of the American Ceramic Society, 93, 3556-3559. Elshazly, E. S., S. M. El-Hout, and M. E. S. Ali, 2011: Yttria Tetragonal Zirconia Biomaterials: Kinetic Investigation. Journal of Materials Science & Technology, 27, 332-337. Fabris, S., A. T. Paxton, and M. W. Finnis, 2002: A stabilization mechanism of zirconia based on oxygen vacancies only. Acta Materialia, 50, 5171-5178. Foster, A. S., V. Sulimov, F. L. Gejo, A. Shluger, and R. M. Nieminen, 2001: Structure and electrical levels of point defects in monoclinic zirconia. Physical Review B, 64, 224108. Francis, J. S., and R. Raj, 2013: Influence of the field and the current limit on flash sintering at isothermal furnace temperatures. Journal of the American Ceramic Society, 96, 2754-2758. Ghosh, S., A. H. Chokshi, P. Lee, and R. Raj, 2009: A Huge Effect of Weak dc Electrical Fields on Grain Growth in Zirconia. Journal of the American Ceramic Society, 92, 1856-1859. Guazzato, M., M. Albakry, S. P. Ringer, and M. V. Swain, 2004: Strength, fracture toughness and microstructure of a selection of all-ceramic materials. Part I. Pressable and alumina glass-infiltrated ceramics. Dental materials : official publication of the Academy of Dental Materials, 20, 441-448. Hsu, Y.-W., K.-H. Yang, K.-M. Chang, S.-W. Yeh, and M.-C. Wang, 2011: Synthesis and crystallization behavior of 3 mol% yttria stabilized tetragonal zirconia polycrystals (3Y-TZP) nanosized powders prepared using a simple co-precipitation process. Journal of Alloys and Compounds, 509, 6864-6870. Inokoshi, M., and Coauthors, 2014: Influence of sintering conditions on low-temperature degradation of dental zirconia. Dental Materials, 30, 669-678. Janek, J., and C. Korte, 1999: Electrochemical blackening of yttria-stabilized zirconia - morphological instability of the moving reaction front. Solid State Ionics, 116, 181-195. Jha, S. K., and Coauthors, 2018: In-situ observation of oxygen mobility and abnormal lattice expansion in ceria during flash sintering. Ceramics Internatinal, 44, 15362-15369. Ji, W., B. Parker, S. Falco, J. Zhang, Z. Fu, and R. Todd, 2017: Ultra-fast firing: Effect of heating rate on sintering of 3YSZ, with and without an electric field. Journal of the European Ceramic Society, 37, 2547-2551. Kakegawa, K., Y. Kawai, Y. Wu, N. Uekawa, and Y. Sasaki, 2004: Sintering of Lead Titanate Using a Spark‐Plasma‐Sintering Technique. Journal of the American Ceramic Society, 87, 541-545. Kaplan, M., A. Ozturk, and J. Park, 2016: Production and Characterization of Yttria Stabilized Zirconia Ceramic Blocks for Dental Applications. Karayannis, V. G., 2016: Microwave sintering of ceramic materials. IOP Conference Series: Materials Science and Engineering, 161, 012068. Kim, S.-W., S. G. Kim, J.-I. Jung, S.-J. L. Kang, I. W. Chen, and J. Roedel, 2011: Enhanced Grain Boundary Mobility in Yttria-Stabilized Cubic Zirconia under an Electric Current. Journal of the American Ceramic Society, 94, 4231-4238. Kim, S. W., S. J. L. Kang, and I. W. Chen, 2013: Electro‐sintering of yttria‐stabilized cubic zirconia. Journal of the American Ceramic Society, 96, 1398-1406. Kobayashi, K., H. Kuwajima, and T. Masaki, 1981: Phase change and mechanical properties of ZrO2-Y2O3 solid electrolyte after ageing. Solid State Ionics, 3, 489-493. Lóh, N. J., L. Simão, C. A. Faller, A. De Noni, and O. R. K. Montedo, 2016: A review of two-step sintering for ceramics. Ceramics International, 42, 12556-12572. Lebrun, J. M., and Coauthors, 2017: In‐situ measurements of lattice expansion related to defect generation during flash sintering. Journal of the American Ceramic Society, 100, 4965-4970. Liu, G. X., D. G. Liu, J. L. Liu, Y. Gao, and Y. G. Wang, 2018: Asymmetric temperature distribution during steady stage of flash sintering dense zirconia. Journal of the European Ceramic Society, 38, 2893-2896. Lucas, T. J., N. C. Lawson, G. M. Janowski, and J. O. Burgess, 2015: Effect of grain size on the monoclinic transformation, hardness, roughness, and modulus of aged partially stabilized zirconia. Dental materials : official publication of the Academy of Dental Materials, 31, 1487-1492. Lughi, V., and V. Sergo, 2010: Low temperature degradation -aging- of zirconia: A critical review of the relevant aspects in dentistry. Dental materials : official publication of the Academy of Dental Materials, 26, 807-820. Menezes, R. R., P. M. Souto, and R. H. G. A. Kiminami, 2012: . Croatia. Muccillo, R., and E. N. S. Muccillo, 2015: Light emission during electric field-assisted sintering of electroceramics. Journal of the European Ceramic Society, 35, 1653-1656. Munir, Z. A., U. Anselmi-Tamburini, and M. Ohyanagi, 2006: The effect of electric field and pressure on the synthesis and consolidation of materials: A review of the spark plasma sintering method. Journal of Materials Science, 41, 763-777. Naik, K. S., V. M. Sglavo, and R. Raj, 2014a: Flash sintering as a nucleation phenomenon and a model thereof. Journal of the European Ceramic Society, 34, 4063-4067. Naik, K. S., V. M., & Raj, R. (2014). Field assisted sintering of ceramic constituted by alumina and yttria stabilized zirconia. Journal of the European Ceramic Society, 34(10), 2435-2442. Narayan, J., 2013: A new mechanism for field-assisted processing and flash sintering of materials. Scripta Materialia, 69, 107-111. Nie, J., Y. Zhang, J. M. Chan, R. Huang, and J. Luo, 2018: Water-assisted flash sintering: flashing ZnO at room temperature to achieve~ 98% density in seconds. Scripta Materialia, 142, 79-82. Presenda, Á., M. D. Salvador, F. L. Peñaranda-Foix, R. Moreno, and A. Borrell, 2015: Effect of microwave sintering on microstructure and mechanical properties in Y-TZP materials used for dental applications. Ceramics International, 41, 7125-7132. Qin, W., H. Majidi, J. Yun, K. van Benthem, and L. Gauckler, 2016: Electrode Effects on Microstructure Formation During FLASH Sintering of Yttrium-Stabilized Zirconia. Journal of the American Ceramic Society, 99, 2253-2259. Raikova, G., P. Carpanese, Z. Stoynov, D. Vladikova, M. Viviani, and A. Barbucci, 2009: Inductance correction in impedance studies of solid oxide fuel cells. In Memoriam, 198. Raj, R., 2012: Joule heating during flash-sintering. Journal of the European Ceramic Society, 32, 2293-2301. Raj, R. (2016). Analysis of the power density at the onset of flash sintering. Journal of the American Ceramic Society, 99(10), 3226-3232.. Ren, K., J. Xia, and Y. Wang, 2019: Grain growth kinetics of 3 mol.% yttria-stabilized zirconia during flash sintering. Journal of the European Ceramic Society, 39, 1366-1373. Rice, R. W., C. C. Wu, and F. Boichelt, 1994: Hardness–grain‐size relations in ceramics. Journal of the American ceramic society, 77, 2539-2553. SATO, T., and M. SHIMADA, 1985: Transformation of yttria‐doped tetragonal ZrO2 polycrystals by annealing in water. Journal of the American Ceramic Society, 68, 356-356. Sinhamahapatra, A., J. P. Jeon, J. Kang, B. Han, and J. S. Yu, 2016: Oxygen-Deficient Zirconia (ZrO2-x): A New Material for Solar Light Absorption. Scientific Reports, 6. Steil, M. C., D. Marinha, Y. Aman, J. R. C. Gomes, and M. Kleitz, 2013: From conventional ac flash-sintering of YSZ to hyper-flash and double flash. Journal of the European Ceramic Society, 33, 2093-2101. Terauds, K., J.-M. Lebrun, H.-H. Lee, T.-Y. Jeon, S.-H. Lee, J. H. Je, and R. Raj, 2015: Electroluminescence and the measurement of temperature during Stage III of flash sintering experiments. Journal of the European Ceramic Society, 35, 3195-3199. Todd, R. I., E. Zapata-Solvas, R. S. Bonilla, T. Sneddon, and P. R. Wilshaw, 2015: Electrical characteristics of flash sintering: thermal runaway of Joule heating. Journal of the European Ceramic Society, 35, 1865-1877. Tokita, M., 1999: Development of Large-Size Ceramic/Metal Bulk FGM Fabricated by Spark Plasma Sintering. Materials Science Forum, 308-311, 83-88. Yoon, B., D. Yadav, R. Raj, E. Sortino, S. Ghose, P. Sarin, and D. Shoemaker, 2018: Measurement of O and Ti atom displacements in TiO2 during flash sintering experiments. Journal of the American Ceramic Society, 101, 1811-1817. Yoshida, H., P. Biswas, R. Johnson, and M. K. Mohan, 2017: Flash‐sintering of magnesium aluminate spinel (MgAl2O4) ceramics. Journal of the American Ceramic Society, 100, 554-562. Yoshida, H., Y. Sakka, T. Yamamoto, J.-M. Lebrun, and R. Raj, 2014: Densification behaviour and microstructural development in undoped yttria prepared by flash-sintering. Journal of the European Ceramic Society, 34, 991-1000. Yoshida, H., K. Morita, B.-N. Kim, Y. Sakka, and T. Yamamoto, 2016: Reduction in sintering temperature for flash-sintering of yttria by nickel cation-doping. Acta Materialia, 106, 344-352. Yu, M., S. Grasso, R. McKinnon, T. Saunders, and M. J. Reece, 2016: Review of flash sintering: materials, mechanisms and modelling. Advances in Applied Ceramics, 116, 24-60. Zapata-Solvas, E., S. Bonilla, P. R. Wilshaw, and R. I. Todd, 2013: Preliminary investigation of flash sintering of SiC. Journal of the European Ceramic Society, 33, 2811-2816. Zhang, Y., and J. Luo, 2015: Promoting the flash sintering of ZnO in reduced atmospheres to achieve nearly full densities at furnace temperatures of< 120 C. Scripta Materialia, 106, 26-29. Zhang, Y., J.-I. Jung, and J. Luo, 2015: Thermal runaway, flash sintering and asymmetrical microstructural development of ZnO and ZnO–Bi2O3 under direct currents. Acta Materialia, 94, 87-100. Zhuang, Y. X., Z. Y. Zhu, T. Jiao, and J. Sun, 2019: Effect of Aging Time and Thickness on Low-Temperature Degradation of Dental Zirconia. Journal of Prosthodontics-Implant Esthetic and Reconstructive Dentistry, 28, E404-E410. | |
dc.identifier.uri | http://tdr.lib.ntu.edu.tw/jspui/handle/123456789/73724 | - |
dc.description.abstract | 陶瓷工業發展至今,除了早期的陶瓷藝品,近年精密陶瓷根據其不同功能性更是廣為運用在諸多領域之中。因此,相較於傳統燒結製備陶瓷的方式,許多快速燒結陶瓷方式被提出,像是微波燒結法以及電漿燒結法。但這些方法受限於材料種類或是設備結構過於複雜,未獲廣泛應用;直到2010瞬閃燒結首度被提出後,透過單純外部電場輔助,可大幅降低燒結溫度與時間,被視為快速燒結中具備量產陶瓷之潛能。
瞬閃燒結大致上可分為主要的三階段,第一階段為固定壓時期,此時只有非常微小的電流通過樣品,同時也被稱為孵育期,用以引發瞬閃燒結的時期。接著依照不同材料,直到數秒鐘至數分鐘不等,電流突然急遽增加達到預設值的上限,此瞬間亦會放出亮光,稱為第二階段。在這短時間內,樣品也會瞬間近乎燒結完成達到緻密化。而後電源輸出轉為定電流模式,維持電源的穩定輸出,完成瞬閃燒結。 由於瞬閃燒結可以大幅降低燒結溫度與時間,能避免相較於傳統燒結中高溫使擴散加速的現象,而導致晶粒成長顯著。因此,瞬閃燒結可製備出具有較小粒徑尺寸且緻密化的陶瓷。在牙瓷材料中目前大多採用氧化鋯,但人體口腔內潮濕環境使得氧化鋯低溫裂化成為主要問題。本研究使用瞬閃燒結法製備摻有氧化釔穩定之氧化鋯(YSZ)用於牙瓷,抑制形成過大的晶粒,同時增強其機械強度。另外,本研究利用瞬閃燒結製備之YSZ成品進行老化檢測,確認相變化未發生,有效避免低溫裂化情形,預期增長使用壽命。 瞬閃燒結提出至今,諸多研究希望藉由釐清其燒結機制,以利此技術後續推廣成熟。目前主要分為三大解釋,第一是來自電場輸出的焦耳熱使得樣品本身溫度較高,得以達到快速擴散結果,但主要發生在二、三階段。而第二種理論是在第一階段時期電場主要用以提高材料缺的濃度,以誘發瞬閃暫態。第三種機制是根據實驗結果發現兩側晶粒尺寸分佈不對稱,認為與電化學還原現象相關,導致還原後的陽離子具有更高的擴散能力,同時氧空位在陰極累積形成孔洞。本研究利用真空環境中進行瞬閃燒結實驗,驗證外部氧氣並非瞬閃燒結必要條件,同時觀察到微小晶粒析出,且確認樣品表面變黑區域為部份還原之氧化鋯。因此,提出瞬閃燒結過程應有電化學氧化還原反應牽涉其中,第一階段為孵育部份還原氧化鋯之時期,待貫穿內部材料後,其高導電性可提供瞬閃燒結進入二三階段之定電流模式。透過部分還原氧化鋯提供瞬閃燒結樣品的導電性後,增強的電場輸出能量得以加速擴散現象導致樣品燒結緻密化。 | zh_TW |
dc.description.abstract | Apart from artistic ceramics in early stage, advanced ceramics has been widely used in different applications according to their functions along with development of ceramics industry. Thus, comparing to conventional sintering method of ceramics, lots of rapid sintering methods had been proposed like microwave sintering and spark plasma sintering. However, some development of these rapid sintering methods were limited by categories of materials or complicated sintering structure. Until flash sintering was first reported in 2012, it had potential for commercial manufacturing ceramics among these rapid sintering with lowering sintering temperature and sintering time by only assisting external electric field.
There are three stages during flash sintering. Stage I is for constant voltage period with only tiny current through specimen, and also called as incubation period to induce flash event. Then depending on different materials, after seconds to several minutes, current would abruptly surge to the pre-setting upper limit with flash event and these called stage II. In this short period, specimen was almost densified instantaneously. Then, output of electric field would turn to constant current mode and maintain the stable dissipation, and finally finish the flash sintering. Due to lower sintering temperature and shorter sintering time, specimen would be densified with smaller grain size, comparing to conventional sintering in higher sintering temperature resulted in higher diffusion rate and grain growth rate. Most dental material use zirconia. However, low temperature degradation is the main issue for zirconia in the human mouth of humid environment. In this work, we manufacture YSZ for dental application by flash sintering to prevent larger grain size occurred and increase mechanical strength simultaneously. In addition, the specimen under flash sintering method would be conducted with aging test to prevent from low temperature degradation without phase transformation and this specimen would be expected using for longer life. There were lots of literatures worked on mechanism of flash sintering from it was first reported and expect to commercialize flash sintering method in the future. So far, there were three main explanation in flash sintering. One is Joule heating from external electric field output and higher diffusion rate was resulted from higher temperature of specimen. But Joule heating was only attributed during stage II and III. Another explanation is higher concentration of extrinsic defect was nucleated by electric field and then it could induce transient state of flash event. The other explanation is according to experience results of asymmetric grain size distribution between two electrodes. This phenomenon was considered to electrochemical reduction related and resulted in higher diffusion rate of reduced cations and pores produced by accumulation of oxygen vacancies. In this work, we conducted flash sintering in vacuum environment and showed external oxygen is not necessary during flash sintering. In addition, we find some small grains were precipitated and blackening phenomenon on the sample surface of partial reduction zirconia. Therefore, we consider electrochemical redox reaction was involved in flash sintering. Stage one is for incubation of partial reduction zirconia. Until partial reduction zirconia penetrated the core of specimen, its high conductivity could offer a path for steady current during stage II and III in flash sintering. Through high conductivity of specimen, larger output energy of electric field could densified specimen rapidly with higher diffusion rate. | en |
dc.description.provenance | Made available in DSpace on 2021-06-17T08:08:49Z (GMT). No. of bitstreams: 1 ntu-108-R06631021-1.pdf: 6953646 bytes, checksum: c490fb61a38d4d87d10213fc764ae392 (MD5) Previous issue date: 2019 | en |
dc.description.tableofcontents | 第一章 前言 1
1.1研究動機 1 1.2研究目的 2 第二章 文獻探討 4 2.1牙瓷材料 4 2.1.1牙瓷簡介 4 2.2 陶瓷燒結方法 6 2.2.1 傳統燒結 6 2.2.2 場輔助燒結 6 2.3 瞬閃燒結法 8 2.3.1瞬閃燒結實驗首次提出 8 2.3.2瞬閃燒結實驗架設 9 2.3.3瞬閃燒結現象 10 2.3.4瞬閃燒結實驗結果現象 12 2.4瞬閃燒結可能機制探討 15 2.4.1焦耳熱 (Joule heating) 17 2.4.2液相燒結 18 2.4.3內部缺陷產生 19 2.4.3擴散活化能降低 21 2.4.4兩極的電化學還原反應 24 2.5 YSZ材料電化學還原現象 25 2.6 部分還原氧化鋯(Oxygen-Deficient Zirconia, ZrO2-x) 27 第三章 材料與方法 31 3.1研究流程 31 3.2製備3YSZ生胚 32 3.2.1粉末選用 34 3.2.2生胚成型 34 3.3瞬閃燒結實驗架設 38 3.4瞬閃燒結製備牙瓷材料 40 3.4.1 瞬閃燒結製備牙瓷材料溫度 44 3.4.2瞬閃燒結製備牙瓷材料電場強度 44 3.4.3里氏硬度量測 45 3.4.4奈米壓痕試驗 45 3.5瞬閃燒結機制探討 46 3.6瞬閃燒結頻譜阻抗分析 49 3.7瞬閃燒結樣品基本特性分析 52 3.7.1真實密度 53 3.7.2相對密度 54 第四章 結果與討論 55 4.1生胚(3YSZ)材料分析 55 4.2瞬閃燒結實驗 56 4.3瞬閃燒結製備牙瓷材料 59 4.3.1瞬閃燒結定溫溫度 59 4.3.2瞬閃燒結電場強度 61 4.3.3瞬閃燒結成品進行老化檢測 66 4.4瞬閃燒結機制實驗探討 67 4.4.1瞬閃燒結現象與文獻比較 67 4.4.2瞬閃燒結機制假設 70 4.4.3真空瞬閃燒結實驗結果 71 4.4.4瞬閃燒結於真空與大氣中之差異 80 4.5瞬閃燒結機制理論 84 4.5.1瞬閃燒結機制理論假設 84 4.5.1阻抗分析驗證機制 89 第五章 結論 98 5.1結論 98 5.2未來展望 99 第六章 參考文獻 100 | |
dc.language.iso | zh-TW | |
dc.title | 瞬閃燒結機制探討及其於牙瓷製備之應用 | zh_TW |
dc.title | Flash Sintering Mechanism Exploration and application to Dental Utilization | en |
dc.type | Thesis | |
dc.date.schoolyear | 107-2 | |
dc.description.degree | 碩士 | |
dc.contributor.oralexamcommittee | 段維新,廖國基,黃心豪 | |
dc.subject.keyword | 瞬閃燒結,陶瓷,燒結,氧化釔穩定氧化鋯,電化學反應,牙瓷, | zh_TW |
dc.subject.keyword | Flash Sintering,Ceramic,Sintering,YSZ,Electrochemical reacitons,Dental Utilization, | en |
dc.relation.page | 109 | |
dc.identifier.doi | 10.6342/NTU201903488 | |
dc.rights.note | 有償授權 | |
dc.date.accepted | 2019-08-17 | |
dc.contributor.author-college | 生物資源暨農學院 | zh_TW |
dc.contributor.author-dept | 生物環境系統工程學研究所 | zh_TW |
顯示於系所單位: | 生物環境系統工程學系 |
文件中的檔案:
檔案 | 大小 | 格式 | |
---|---|---|---|
ntu-108-1.pdf 目前未授權公開取用 | 6.79 MB | Adobe PDF |
系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。