標題: | Hf添加入Ti-30Nb-1Fe與Ti-40Nb合金
於電化學腐蝕行為之探討 Effects of Hf content on electrochemical corrosion behavior of biomedical Ti-30Nb-1Fe and Ti-40Nb alloys |
作者: | Shoa-Hui Chiou 邱少暉 |
指導教授: | 潘永寧(Yong-ning Pan) |
關鍵字: | Ti-30Nb-1Fe-xHf`,Ti-40Nb-yHf, |
出版年 : | 2010 |
學位: | 碩士 |
摘要: | 本研究針對不同Hf含量(1~4%)之Ti-30Nb-1Fe-xHf與Ti-40Nb-yHf生醫用合金,分別在0.9%NaCl(pH 5.6)與0.2%NaF(pH 4)溶液中,以極化試驗及浸泡試驗來探討合金之耐腐蝕性質,並以掃描式電子顯微鏡觀察合金浸泡於含氟離子溶液後之表面形貌,再以X光電子能譜儀分析合金於含氟離子浸泡試驗後之表面之化學組成。 研究結果指出,Ti-30Nb-1Fe-xHf合金之抗腐蝕能力以Ti-30Nb-1Fe-1Hf最佳;Ti-40Nb-yHf合金之抗腐蝕能力則無明顯差異。觀察合金浸泡於含氟離子溶液之表面形貌,推論Ti-30Nb-1Fe-xHf合金其腐蝕行為屬於選擇性腐蝕(selective corrosion),而Ti-40Nb-yHf合金其腐蝕行為屬於均勻性腐蝕(uniform corrosion)。另外,合金浸泡後的表面化學組成為氫氧化物與TiO2及Nb2O5組成之金屬氧化物,但並無發現相關之氟化物。 The purpose of this research is to investigate the electrochemical corrosion behaviros of Ti-30Nb-1Fe-xHf and Ti-40-Nb-yHf (x, y= 1, 2, 3, and 4 wt%) alloys in 0.9%NaCl (pH=5.6) and 0.2%NaF (pH=4.0) solutions, utilizing potentiodynamic polarization and immerse tests. After testing, the surfaces of the alloys were examined by scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). The results reveal that the corrosion resistance of Ti-30Nb-1Fe-1Hf alloy is the best among Ti-30Nb-1Fe-xHf alloys studied. Whereas, for Ti-40-Nb-yHf alloys, no significant difference in corrosion resistance can be obtained with different Hf content. The analyses of surface morphologies of the Ti-30Nb-1Fe-xHf alloys after immersed in flouride solution suggest that the corrosion behavior is a selective type. On the other hand, a uniform corrosion mode is responsible for Ti-40-Nb-yHf alloys. The constituents on the surfaces of both types of alloy consist of hydroxide, TiO2 and Nb2O5, but not fluoride. |
URI: | http://tdr.lib.ntu.edu.tw/jspui/handle/123456789/47833 |
全文授權: | 有償授權 |
顯示於系所單位: | 機械工程學系 |
文件中的檔案:
檔案 | 大小 | 格式 | |
---|---|---|---|
ntu-99-1.pdf 目前未授權公開取用 | 4.82 MB | Adobe PDF |
系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。