DC 欄位 | 值 | 語言 |
---|---|---|
dc.contributor.advisor | 楊志忠(Chih-Chung Yang) | |
dc.contributor.author | Yu-Ren Lin | en |
dc.contributor.author | 林育任 | zh_TW |
dc.date.accessioned | 2021-06-07T18:16:21Z | - |
dc.date.copyright | 2020-08-04 | |
dc.date.issued | 2020 | |
dc.date.submitted | 2020-07-29 | |
dc.identifier.citation | 1.M. Kneissl, T. Kolbe, C. Chua, V. Kueller, N. Lobo, J. Stellmach, A. Knauer, H. Rodriguez, S. Einfeldt, and Z. Yang, “Advances in group III-nitride-based deep UV light-emitting diode technology,” Semicond. Sci. Technol. 26, 014036 (2011). 2.T. F. Kent, S. D. Carnevale, A. T. M. Sarwar, P. J. Phillips, R. F. Klie, and R. C. Myers, “Deep ultraviolet emitting polarization induced nanowire light emitting diodes with AlxGa1-xN active regions,” Nanotechnology 25, 455201 (2014). 3.M. Shatalov, W. Sun, A. Lunev, X. Hu, A. Dobrinsky, Y. Bilenko, J. Yang, M. Shur, R. Gaska, C. Moe, G. Garrett, and M. Wraback, “AlGaN deep-ultraviolet light-emitting diodes with external quantum efficiency above 10%,” Appl. Phys. Express 5, 082101 (2012). 4.T. Takano, T. Mino, J. Sakai, N. Noguchi, K. Tsubaki, and H. Hirayama, “Deep-ultraviolet light-emitting diodes with external quantum efficiency higher than 20% at 275 nm achieved by improving light-extraction efficiency,” Appl. Phys. Express 10, 031002 (2017). 5.H. Hirayama, Y. Tsukada, T. Maeda, and N. Kamata, “Marked enhancement in the efficiency of deep-ultraviolet AlGaN light-emitting diodes by using a multiquantum-barrier electron blocking layer,” Appl. Phys. Express 3, 031002 (2010). 6.D. J. Kim and D. Y. Ryu, N. A. Bojarczuk, J. Karasinski, S. Guha, S. H. Lee, and J. H. Lee, “Thermal activation energies of Mg in GaN:Mg measured by the Hall effect and admittance spectroscopy,” J. Appl. Phys. 88, 2564 (2000). 7.K. B. Nam, M. L. Nakarmi, J. Li, J. Y. Lin, and H. X. Jiang, “Mg acceptor level in AlN probed by deep ultraviolet photoluminescence,”Appl. Phys. Lett. 83, 878 (2003). 8.M. Zhong, J. Roberts, W. Kong, A. S. Brown, and A. J. Steckl, “p-type GaN grown by phase shift epitaxy,” Appl. Phys. Lett. 104, 012108 (2014). 9.M. L. Nakarmi, K. H. Kim, J. Li, J. Y. Lin, and H. X. Jiang, “Enhanced p-type conduction in GaN and AlGaN by Mg-δ-doping,” Appl. Phys. Lett. 82, 3041 (2003). 10.Y. Chen, H. Wu, E. Han, G. Yue, Z. Chen, Z. Wu, G. Wang, and H. Jiang, “High hole concentration in p-type AlGaN by indium-surfactant-assisted Mg-delta doping,” Appl. Phys. Lett. 106, 162102 (2015). 11.C. Bayram, J. L. Pau, R. McClintock, and M. Razeghi, “Delta-doping optimization for high quality p-type GaN,” J. Appl. Phys. 104, 083512 (2008). 12.Y. Chen, H. Wu, G. Yue, Z. Chen, Z. Zheng, Z. Wu, G. Wang, H. Jiang, “Enhanced Mg doping efficiency in p-type GaN by indium-surfactant- assisted delta doping method,” Appl. Phys. Express 6, 041001 (2013). 13.E. C. H. Kyle, S. W. Kaun, E. C. Young, and J. S. Speck, “Increased p-type conductivity through use of an indium surfactant in the growth of Mg-doped GaN,” Appl. Phys. Lett. 106, 222103 (2015). 14.B. Sarkar, S. Mita, P. Reddy, A. Klump, F. Kaess, J. Tweedie, I. Bryan, Z. Bryan, R. Kirste, E. Kohn, R. Collazo, and Z. Sitar, “High free carrier concentration in p-GaN grown on AlN substrates,” Appl. Phys. Lett. 111, 032109 (2017). 15.M. L. Nakarmi, K. H. Kim, J. Li, J. Y. Lin, and H. X. Jiang, “Enhanced p-type conduction in GaN and AlGaN by Mg-δ-doping,” Appl. Phys. Lett. 82, 3041 (2003). 16.K. B. Nam, M. L. Nakarmi, J. Li, J. Y. Lin, and H. X. Jiang, “Mg acceptor level in AlN probed by deep ultraviolet photoluminescence,”Appl. Phys. Lett. 83, 878 (2003). 17.T. Kinoshita, T.Obata, H. Yanagi, and S. I. Inoue, “High p-type conduction in high-Al content Mg-doped AlGaN,” Appl. Phys. Lett. 102, 012105 (2013). 18.Y. Chen, H. Wu, E. Han, G. Yue, Z. Chen, Z. Wu, G. Wang, and H. Jiang, “High hole concentration in p-type AlGaN by indium-surfactant-assisted Mg-delta doping,” Appl. Phys. Lett. 106, 162102 (2015). 19.Y. H. Liang, N. T. Nuhfer, and E. Towe, “Liquid-metal-enabled synthesis of aluminum-containing III-nitrides by plasma-assisted molecular beam epitaxy,” J. Vac. Sci. Technol. B 34, 02L112 (2016). 20.Y. H. Liang and E. Towe, “Heavy Mg-doping of (Al,Ga)N films for potential applications in deep ultraviolet light-emitting structures,” Journal of Applied Physics 123, 095303 (2018). 21.X. Liu, A. Pandey, D. A. Laleyan, K. Mashooq, E. T. Reid, W. J. Shin and Z. Mi, “Charge carrier transport properties of Mg-doped Al0.6Ga0.4N grown by molecular beam epitaxy,” Semicond. Sci. Technol. 33, 085005 (2018). 22.W. Luo, B. Liu, Z. Li, Liang Li, Q. Yang, L. Pan, C. Li, D. Zhang, X. Dong, D. Peng, F. Yang, and R. Zhang, “Enhanced p-type conduction in AlGaN grown by metal-source flow-rate modulation epitaxy,” Appl. Phys. Lett. 113, 072107 (2018). 23.D. C. Look and R. J. Molnar, “Degenerate layer at GaN/sapphire interface: Influence on Hall-effect measurements,” Appl. Phys. Lett. 70, 3377 (1997). 24.D. C. Look, E. R. Heller, Y. F. Yao, and C. C. Yang, “Significant mobility enhancement in extremely thin highly doped ZnO films,” Appl. Phys. Lett. 106, 152102 (2015). 25.P. Kozodoy, Y. P. Smorchkova, M. Hansen, H. Xing, S. P. DenBaars, U. K. Mishra, A. W. Saxler, R. Perrin, and W. C. Mitchel, “Polarization-enhanced Mg doping of AlGaN/GaN superlattices,” Appl. Phys. Lett. 75, 2444 (1999). 26.E. L. Waldron, J. W. Graff, and E. F. Schubert, “Improved mobilities and resistivities in modulation-doped p-type AlGaN/GaN superlattices,” Appl. Phys. Lett. 79, 2737 (2001). 27.J. Hertkorn, S. B. Thapa, T. Wunderer, F. Scholz, Z. H. Wu, Q. Y. Wei, F. A. Ponce, M. A. Moram, C. J. Humphreys, C. Vierheilig, and U. T. Schwarz, “Highly conductive modulation doped composition graded p-AlGaN/(AlN)/GaN multiheterostructures grown by metalorganic vapor phase epitaxy,” J. Appl. Phys. 106, 013720 (2009). 28.J. Simon, V. Protasenko, C. Lian, H. Xing, and D. Jena, “Polarization-induced hole doping in wide-Band-gap uniaxial semiconductor heterostructures,” Science 327, 60 (2010). 29.S. Li, M. E. Ware, V. P. Kunets, M. Hawkridge, P. Minor, J. Wu, and G. J. Salamo, “Polarization induced doping in graded AlGaN films,” Phys. Status Solidi C 8, No. 7–8, 2182–2184 (2011). 30.S. Li, M. Ware, J. Wu, P. Minor, Z. Wang et al, “Polarization induced pn-junction without dopant in graded AlGaN coherently strained on GaN,” Appl. Phys. Lett. 101, 122103 (2012). 31.S. Li, T. Zhang, J. Wu, Y. Yang, Z. Wang, Z. Wu, Z. Chen, and Y. Jiang, “Polarization induced hole doping in graded AlxGa1-xN (x=0.7~1) layer grown by molecular beam epitaxy,” Appl. Phys. Lett. 102, 062108 (2013). 32.P. M. Lytvyn, A. V. Kuchuk, Y. I. Mazur, C. Li, M. E. Ware, Z. M. Wang, V. P. Kladko, A. E. Belyaev, and G. J. Salamo, “Polarization Effects in Graded AlGaN Nanolayers Revealed by Current-Sensing and Kelvin Probe Microscopy,” ACS Appl. Mater. Interfaces, 10, 6755−6763 (2018). 33.H. T. Chen, C. Y. Su, C. G. Tu, Y. F. Yao, C. H. Lin, Y. R. Wu, Y. W. Kiang, and C. C. Yang, “Combining high hole concentration in p-GaN and high mobility in u-GaN for high p-type conductivity in a p-GaN/u-GaN alternating-layer nanostructure,” IEEE Transact. Electron Dev. 64, 115 (2017). 34.Y. F. Yao, H. T. Chen, Y. Kuo, C. Y. Su, C. G. Tu, C. H. Lin, Y. W. Kiang, and C. C. Yang, “Current penetration depth and effective conductivity of a nano-scale p-GaN/u-GaN alternating-layer p-type structure,” Superlattices and Microstructures 124, 107 (2018). 35.C. Y. Huang, K. S. Chang, C. Y. Huang, Y. H. Lin, W. C. Peng, H. W. Yen, R. M. Lin, and H. C. Kuo, “The origin and mitigation of volcano-like morphologies in micron-thick AlGaN/AlN heteroepitaxy,” Appl. Phys . Lett. 111, 072110 (2017). | |
dc.identifier.uri | http://tdr.lib.ntu.edu.tw/jspui/handle/123456789/16470 | - |
dc.description.abstract | 我們利用分子束磊晶技術,在氮化鎵基板上成長七個鋁含量約25%不同結構的氮化鋁鎵樣品,並比較樣品之間的p-型導電特性。其中,相較於均勻鎂摻雜氮化鋁鎵樣品,其他六個奈米尺度的鎂摻雜/無摻雜氮化鋁鎵交替層結構樣品皆具有較高的導電率。由於無摻雜氮化鋁鎵層內電洞遷移率大於鎂摻雜氮化鋁鎵層,而交替層結構內鎂摻雜氮化鋁鎵層所產生的電洞可以擴散至相鄰的無摻雜氮化鋁鎵層中,並以較大的電洞遷移率傳輸,因而可以改善樣品整體的導電特性。一般而言,交替層結構樣品的導電率會隨著分層厚度減少而增加;然而,樣品內鎂摻雜和無摻雜氮化鋁鎵層的相對厚度也會影響其導電特性。我們發現鎂摻雜與無摻雜氮化鋁鎵分層厚度分別為6奈米與4奈米的交替層結構樣品的等效電阻率比均勻鎂摻雜氮化鋁鎵樣品降低了4.7-6.5倍。此外,我們也建立一套模型來釐清無摻雜氮化鋁鎵內電洞遷移率以及擴散至無摻雜氮化鋁鎵層的電洞比率兩者間的關係。 | zh_TW |
dc.description.abstract | Based on molecular beam epitaxy, seven AlGaN samples of ~25 % Al content on GaN templates are prepared for comparing their p-type behaviors. In particular, six nm-scale p-AlGaN/u-AlGaN layer-structure samples are grown to show the higher sheet conductance levels, when compared with a uniform p-AlGaN thick-layer sample. The higher conductance in a layer-structure sample is caused by the diffusion of holes generated in a p-AlGaN layer into the neighboring u-AlGaN layers, in which hole mobility is significantly higher when compared with that in a p-AlGaN layer. The sheet conductance in a layer-structure sample generally increases with decreasing layer thickness. However, it is also controlled by the relative thicknesses of the p-AlGaN and u-AlGaN layers. In the layer-structure sample of 6 (4) nm for the p-AlGaN (u-AlGaN) layer thickness, the effective resistivity is reduced by a factor of 4.7-6.5, when compared to that of the uniform p-AlGaN sample. A simple model is built for understanding the relation between the hole mobility in u-AlGaN and the fraction of holes diffused into the u-AlGaN layers. | en |
dc.description.provenance | Made available in DSpace on 2021-06-07T18:16:21Z (GMT). No. of bitstreams: 1 U0001-2807202017305900.pdf: 2235176 bytes, checksum: a593de60c55e28d190b58aa56b33bba6 (MD5) Previous issue date: 2020 | en |
dc.description.tableofcontents | 致謝.............................................................................i 中文摘要........................................................................ ii Abstract........................................................................iii Content.........................................................................iv List of figure..................................................................vi List of table...................................................................ix Chapter 1 Introduction..........................................................1 1.1 Ultraviolet light-emitting diode............................................1 1.2 Development of p-type AlGaN.................................................2 1.3 Polarization induced p-type AlGaN behaviors.................................3 1.4 Improvement of p-GaN conductivity based on an alternating-layer structure...4 1.5 Evaluation of p-type conductivity in an alternating-layer structure.........5 1.6 Growth of Mg-doped AlGaN with molecular beam epitaxy........................7 1.7 Research motivations........................................................7 1.8 Thesis structure............................................................8 Chapter 2 Sample Structures, Growth Conditions, and Basic Properties............15 2.1 Sample structures and growth conditions.....................................15 2.2 Basic sample properties.....................................................16 Chapter 3 Measurement Results...................................................29 3.1 Secondary ion mass spectroscopy measurement results.........................29 3.2 Hall measurement results....................................................30 Chapter 4 Modeling and Discussions..............................................41 4.1 Modeling....................................................................41 4.2 Estimations based on the model..............................................42 4.3 Discussions.................................................................44 Chapter 5 Conclusions...........................................................50 References......................................................................51 | |
dc.language.iso | en | |
dc.title | 利用鎂摻雜/無摻雜氮化鋁鎵交替層結構來改善p-型氮化鋁鎵的導電特性 | zh_TW |
dc.title | Improvement of p-type AlGaN Conductivity with an Alternating Mg-doped/un-doped AlGaN Layer Structure | en |
dc.type | Thesis | |
dc.date.schoolyear | 108-2 | |
dc.description.degree | 碩士 | |
dc.contributor.oralexamcommittee | 林浩雄(Hao-Hsiung Lin),黃建璋(Jian-Jang Huang),陳奕君(I-Chun Cheng),吳育任(Yuh-Renn Wu) | |
dc.subject.keyword | p-型氮化鋁鎵,分子束磊晶,交替層結構, | zh_TW |
dc.subject.keyword | p-type AlGaN,MBE,Alternating layer structure, | en |
dc.relation.page | 54 | |
dc.identifier.doi | 10.6342/NTU202001984 | |
dc.rights.note | 未授權 | |
dc.date.accepted | 2020-07-29 | |
dc.contributor.author-college | 電機資訊學院 | zh_TW |
dc.contributor.author-dept | 光電工程學研究所 | zh_TW |
顯示於系所單位: | 光電工程學研究所 |
文件中的檔案:
檔案 | 大小 | 格式 | |
---|---|---|---|
U0001-2807202017305900.pdf 目前未授權公開取用 | 2.18 MB | Adobe PDF |
系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。